In order to obtain the optimal PVDF piezoelectric fiber film to enhance its piezoelectric properties, PVDF was used as solute, N–N dimethylformamide (DMF) and acetone were used as solvents, and the electrospinning process parameters and electrode corona were optimized. Based on the control variable method, the effects of solvent ratio (volume ratio of DMF to acetone), solution concentration, spinning voltage, solution injection speed and receiving drum speed on the performance of PVDF piezoelectric fiber membrane were studied and analyzed. The characterization results of the viscosity of PVDF solution, the microstructure of PVDF piezoelectric fiber membrane, the content of crystal phase, the piezoelectric constant, the tensile strength and the dielectric constant after silver electrode were measured. The optimal preparation process parameters of PVDF piezoelectric membrane were obtained: solvent ratio 6:4, solution concentration 15%, spinning voltage 21.5 kV, solution injection speed 0.04 mm/min and receiving drum speed 1800 rpm.

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Preparation of PVDF Fiber Membrane and Optimization of Process Parameters

  • 会议论文

  • 发表日期：

    2025年

查看全文
  • Jie Mei,
  • Xufeng Ji,
  • Xianliang Huang,
  • Wanjie Chen,
  • Dingfang Chen

摘要

In order to obtain the optimal PVDF piezoelectric fiber film to enhance its piezoelectric properties, PVDF was used as solute, N–N dimethylformamide (DMF) and acetone were used as solvents, and the electrospinning process parameters and electrode corona were optimized. Based on the control variable method, the effects of solvent ratio (volume ratio of DMF to acetone), solution concentration, spinning voltage, solution injection speed and receiving drum speed on the performance of PVDF piezoelectric fiber membrane were studied and analyzed. The characterization results of the viscosity of PVDF solution, the microstructure of PVDF piezoelectric fiber membrane, the content of crystal phase, the piezoelectric constant, the tensile strength and the dielectric constant after silver electrode were measured. The optimal preparation process parameters of PVDF piezoelectric membrane were obtained: solvent ratio 6:4, solution concentration 15%, spinning voltage 21.5 kV, solution injection speed 0.04 mm/min and receiving drum speed 1800 rpm.