<p>A comprehensive investigation on the impact mechanisms of biomass blending on coke microstructure and properties was conducted through multi-scale characterization approaches, including X-ray diffraction (XRD), Raman spectroscopy, nitrogen adsorption porosimetry, and scanning electron microscopy (SEM). The results indicate that the introduction of biomass significantly reduces the graphitization degree of coke, as evidenced by the decrease in crystallite size, the increase in interlayer spacing (<i>d</i><sub>002</sub>), and the reduction in aromaticity. Raman spectroscopy analysis further confirms that, with the increase in biomass addition, the <i>I</i><sub>D</sub>/<i>I</i><sub>G</sub> value decreases by 0.15–0.25, indicating a reduction in aromatic hydrocarbons with more than 6 fused rings. Meanwhile, the <i>I</i><sub>D</sub>/(<i>I</i><sub>GR</sub> + <i>I</i><sub>VL</sub> + <i>I</i><sub>VR</sub>) value decreases by 0.3–0.5, suggesting an increase of 15–25% in the proportion of small aromatic systems with 3–5 rings. The impact of different biomasses varies significantly: Poplar leaves, due to their high volatile matter content, exhibit the strongest inhibition of thermal polycondensation. In contrast, bamboo maintains a more ordered structure owing to the supporting effect of its silicon-aluminum framework. Pore analysis indicates that the specific surface area of biomass char increased from 1.5956 m<sup>2</sup>&#xa0;g<sup>–1</sup> without the addition of biomass to 2.0462–2.5356 m<sup>2</sup>&#xa0;g<sup>–1</sup> with the addition of 8% biomass, while the average pore diameter expanded from 4.1459 to 7.4969–9.5383 nm. SEM observations indicate that poplar leaf coke exhibits the highest porosity but also the greatest structural disorder. In contrast, bamboo coke demonstrates the best mesopore connectivity. This study provides theoretical support for optimizing the performance of metallurgical coke through biomass modification.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Influence of Biomass Blending on Metallurgical Performance and Microstructure of Coke

  • 期刊论文

  • 发表日期：

    2025年5月1日

查看全文
  • Yue Duan,
  • Qing-hai Pang,
  • Fu-liang Teng,
  • Zheng-wei Li,
  • Ze-qi Wei,
  • Shuai Liu

摘要

A comprehensive investigation on the impact mechanisms of biomass blending on coke microstructure and properties was conducted through multi-scale characterization approaches, including X-ray diffraction (XRD), Raman spectroscopy, nitrogen adsorption porosimetry, and scanning electron microscopy (SEM). The results indicate that the introduction of biomass significantly reduces the graphitization degree of coke, as evidenced by the decrease in crystallite size, the increase in interlayer spacing (d002), and the reduction in aromaticity. Raman spectroscopy analysis further confirms that, with the increase in biomass addition, the ID/IG value decreases by 0.15–0.25, indicating a reduction in aromatic hydrocarbons with more than 6 fused rings. Meanwhile, the ID/(IGR + IVL + IVR) value decreases by 0.3–0.5, suggesting an increase of 15–25% in the proportion of small aromatic systems with 3–5 rings. The impact of different biomasses varies significantly: Poplar leaves, due to their high volatile matter content, exhibit the strongest inhibition of thermal polycondensation. In contrast, bamboo maintains a more ordered structure owing to the supporting effect of its silicon-aluminum framework. Pore analysis indicates that the specific surface area of biomass char increased from 1.5956 m2 g–1 without the addition of biomass to 2.0462–2.5356 m2 g–1 with the addition of 8% biomass, while the average pore diameter expanded from 4.1459 to 7.4969–9.5383 nm. SEM observations indicate that poplar leaf coke exhibits the highest porosity but also the greatest structural disorder. In contrast, bamboo coke demonstrates the best mesopore connectivity. This study provides theoretical support for optimizing the performance of metallurgical coke through biomass modification.