Objective <p>Enhancing the mechanical properties of composite resins and promoting dentin remineralization are effective strategies for extending the longevity of restorations. In this study, we developed a pH-responsive composite resin reinforced with phosphorylated chitosan (Pchi)/amorphous calcium phosphate (ACP) and amino-functionalized mesoporous silica nanoparticles (MSNs) (Pchi/ACP@A-MSN complexes).</p> Methods <p>MSNs and Pchi/ACP were synthesized, and the resulting composite resins were classified into five groups based on the filler compositions: Group A (45wt.% A-MSNs + 15wt.% Pchi/ACP + 40wt.% resin matrix), Group B (22.5wt.% A-MSNs + 37.5wt.% Pchi/ACP@A-MSNs + 40wt.% resin matrix), Group C (45wt.% nonporous silica + 15wt.% Pchi/ACP + 40wt.% resin matrix), Group D (15wt.% Pchi/ACP + 85wt.% resin matrix), and Group E (100wt.% resin matrix). The degree of double-bond conversion and mechanical properties (Flexural modulus, flexural strength, and Vickers hardness) of each group were measured. The remineralization performance and calcium ion (Ca²⁺) release performance were observed. Cell viability was evaluated by CCK-8 assay.</p> Results <p>Group A exhibited the highest mechanical performance, with flexural strength of 115 ± 9.68&#xa0;MPa, flexural modulus of 5.99 ± 0.44 GPa, and Vickers hardness of 31.73 ± 2.39 HV. All groups achieved double-bond conversion rates &gt; 50% after 60&#xa0;s of light curing (<i>P</i> &gt; 0.05). At pH 4.0, Group B exhibited the highest Ca²⁺ release (276&#xa0;µg/mL), while Group D had the highest release at pH 7.4 (128&#xa0;µg/mL). SEM and EDS analyses indicated that Group D achieved the most substantial dentin remineralization, followed by Groups C and A. All groups maintained cell viability above 75% throughout the 7-day assay, with no significant cytotoxicity observed.</p> Conclusion <p>A composite formulation containing 45 wt% A-MSNs and 15 wt% Pchi/ACP (Group A) significantly enhanced mechanical strength. The 15 wt% Pchi/ACP formulation (Group D) demonstrated the greatest remineralization effect. Group B, combining A-MSNs and Pchi/ACP@A-MSNs, provided pH-responsive Ca²⁺ release with a favorable balance of mechanical performance and remineralization potential. All formulations met the biocompatibility requirements for dental applications.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

pH-Responsive mesoporous silica nanoparticle-reinforced composite resin with remineralization capability

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2025年7月23日

查看全文
  • Yongcheng Ge,
  • Ting Zhao,
  • Yuguang Liu,
  • Sizheng Fan,
  • Pengyuan Liu,
  • Chengji Zhao,
  • Xiaoqiu Liu

摘要

Objective

Enhancing the mechanical properties of composite resins and promoting dentin remineralization are effective strategies for extending the longevity of restorations. In this study, we developed a pH-responsive composite resin reinforced with phosphorylated chitosan (Pchi)/amorphous calcium phosphate (ACP) and amino-functionalized mesoporous silica nanoparticles (MSNs) (Pchi/ACP@A-MSN complexes).

Methods

MSNs and Pchi/ACP were synthesized, and the resulting composite resins were classified into five groups based on the filler compositions: Group A (45wt.% A-MSNs + 15wt.% Pchi/ACP + 40wt.% resin matrix), Group B (22.5wt.% A-MSNs + 37.5wt.% Pchi/ACP@A-MSNs + 40wt.% resin matrix), Group C (45wt.% nonporous silica + 15wt.% Pchi/ACP + 40wt.% resin matrix), Group D (15wt.% Pchi/ACP + 85wt.% resin matrix), and Group E (100wt.% resin matrix). The degree of double-bond conversion and mechanical properties (Flexural modulus, flexural strength, and Vickers hardness) of each group were measured. The remineralization performance and calcium ion (Ca²⁺) release performance were observed. Cell viability was evaluated by CCK-8 assay.

Results

Group A exhibited the highest mechanical performance, with flexural strength of 115 ± 9.68 MPa, flexural modulus of 5.99 ± 0.44 GPa, and Vickers hardness of 31.73 ± 2.39 HV. All groups achieved double-bond conversion rates > 50% after 60 s of light curing (P > 0.05). At pH 4.0, Group B exhibited the highest Ca²⁺ release (276 µg/mL), while Group D had the highest release at pH 7.4 (128 µg/mL). SEM and EDS analyses indicated that Group D achieved the most substantial dentin remineralization, followed by Groups C and A. All groups maintained cell viability above 75% throughout the 7-day assay, with no significant cytotoxicity observed.

Conclusion

A composite formulation containing 45 wt% A-MSNs and 15 wt% Pchi/ACP (Group A) significantly enhanced mechanical strength. The 15 wt% Pchi/ACP formulation (Group D) demonstrated the greatest remineralization effect. Group B, combining A-MSNs and Pchi/ACP@A-MSNs, provided pH-responsive Ca²⁺ release with a favorable balance of mechanical performance and remineralization potential. All formulations met the biocompatibility requirements for dental applications.