Abstract <p>Two methods of liquid-phase synthesis—coprecipitation of hydroxides and co-crystallization of nitrate salts—are used to synthesize highly dispersed mesoporous powder samples. The samples have the following composition: (CeO<sub>2</sub>)<sub>1<i>–x</i></sub>(Dy<sub>2</sub>O<sub>3</sub>)<sub><i>x</i></sub> (<i>x</i> = 0.05, 0.10, 0.15, 0.20) with a specific pore volume ranging between 0.028 and 0.086 cm<sup>3</sup>/g and a specific surface area of 22.68–66.32 m<sup>2</sup>/g. The powder obtained is used to make ceramic nanomaterials having designed composition. These are cubic fluorite type solid solutions having a coherent scattering region (CSR) of ~78–91 nm (1300°C). The open porosity varies between 2 and 14%. The apparent density is fairly high (5.87–7.05 g/cm<sup>3</sup>). Different effects of synthesis conditions influence the physics and chemical properties of the ceramic electrolyte materials. It is shown that the synthesis used to obtain sintering additive ZnO for ceramics controls open porosity and density in different manner: the open porosity drops 3–5 times and the density increases when the salt co-crystallization technique is used. However, it is shown that the porosity exhibits a decrease by 2 times in the samples synthesized using the hydroxide coprecipitation method, which confirms the selective effect of sintering additives. The new ceramic materials have physical and chemical properties (density, porosity, and coefficient of thermal expansion) making them promising for applications as solid oxide electrolytes in medium-temperature fuel cells.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Effects of Xerogel Synthesis on Physical and Chemical Properties of Nanopowder and Ceramic Materials in the CeO2–Dy2O3 System

  • 期刊论文

  • 发表日期：

    2025年9月24日

查看全文
  • M. V. Kalinina,
  • T. V. Khamova,
  • N. V. Farafonov,
  • N. R. Loktyushkin,
  • S. V. Myakin,
  • I. Yu. Kruchinina

摘要

Abstract

Two methods of liquid-phase synthesis—coprecipitation of hydroxides and co-crystallization of nitrate salts—are used to synthesize highly dispersed mesoporous powder samples. The samples have the following composition: (CeO2)1–x(Dy2O3)x (x = 0.05, 0.10, 0.15, 0.20) with a specific pore volume ranging between 0.028 and 0.086 cm3/g and a specific surface area of 22.68–66.32 m2/g. The powder obtained is used to make ceramic nanomaterials having designed composition. These are cubic fluorite type solid solutions having a coherent scattering region (CSR) of ~78–91 nm (1300°C). The open porosity varies between 2 and 14%. The apparent density is fairly high (5.87–7.05 g/cm3). Different effects of synthesis conditions influence the physics and chemical properties of the ceramic electrolyte materials. It is shown that the synthesis used to obtain sintering additive ZnO for ceramics controls open porosity and density in different manner: the open porosity drops 3–5 times and the density increases when the salt co-crystallization technique is used. However, it is shown that the porosity exhibits a decrease by 2 times in the samples synthesized using the hydroxide coprecipitation method, which confirms the selective effect of sintering additives. The new ceramic materials have physical and chemical properties (density, porosity, and coefficient of thermal expansion) making them promising for applications as solid oxide electrolytes in medium-temperature fuel cells.