<p>Polycrystalline samples of rare earth hexaaluminates LaMgAl<sub>11</sub>O<sub>19</sub>, PrMgAl<sub>11</sub>O<sub>19</sub>, NdMgAl<sub>11</sub>O<sub>19</sub>, and SmMgAl<sub>11</sub>O<sub>19</sub> were synthesized by the citrate sol-gel method with subsequent firing of xerogels in air. Thermal expansion of the compounds obtained was studied by the dilatometric method. Continuous shrinkage of samples was measured in the temperature range of 20–1600°C in air. In the temperature range of 20–1500°C, the linear thermal expansion coefficients of sintered ceramic samples of complex oxides LnMgAl<sub>11</sub>O<sub>19</sub> (Ln = La, Pr, Nd, Sm) were determined, the values of which varied from 9.5 × 10<sup>–6</sup> to 12.9 × 10<sup>–6</sup>°C<sup>–1</sup>.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Thermal Expansion of Complex Oxides LaMgAl11O19, PrMgAl11O19, NdMgAl11O19, and SmMgAl11O19

  • 期刊论文

  • 发表日期：

    2025年8月2日

查看全文
  • K. S. Gavrichev,
  • V. N. Guskov,
  • P. G. Gagarin,
  • A. V. Guskov,
  • M. A. Ryumin,
  • Yu. F. Kargin

摘要

Polycrystalline samples of rare earth hexaaluminates LaMgAl11O19, PrMgAl11O19, NdMgAl11O19, and SmMgAl11O19 were synthesized by the citrate sol-gel method with subsequent firing of xerogels in air. Thermal expansion of the compounds obtained was studied by the dilatometric method. Continuous shrinkage of samples was measured in the temperature range of 20–1600°C in air. In the temperature range of 20–1500°C, the linear thermal expansion coefficients of sintered ceramic samples of complex oxides LnMgAl11O19 (Ln = La, Pr, Nd, Sm) were determined, the values of which varied from 9.5 × 10–6 to 12.9 × 10–6°C–1.