Abstract <p>By means of the thermochemical method of wood modification it is possible to achieve a comprehensive improvement of wood properties—to significantly increase its strength properties and hygroscopicity. During deep and through impregnation with a colored solution, wood is colored due to the solution moving inside the wood through the cavities of cells having a tubular structure. Having penetrated inside the wood through the capillaries of vessels, tracheids and medullary rays, the dye colors the cell walls, diffusing into their intercapillary spaces. In this case, the cell walls are colored more intensively than the cell cavities. The increase in the strength of modified wood is explained by insufficient water adsorption due to a decrease in the diameter of tracheids filled with the modifier solution; apparently, this is also associated with a decrease in the contact area with water of the glue–wood boundary layer due to a decrease in the size of the cell cavities. The shear strength along the fibers corresponds to the European standard EN205 D4. The increase in water resistance of modified wood is due to the fact that urea compacts the wood and gives it increased dimensional stability.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

A Study of the Physical and Mechanical Properties of Modified Wood

  • 期刊论文

  • 发表日期：

    2025年3月1日

查看全文
  • N. G. Kolesov,
  • G. S. Varankina,
  • D. S. Rusakov

摘要

Abstract

By means of the thermochemical method of wood modification it is possible to achieve a comprehensive improvement of wood properties—to significantly increase its strength properties and hygroscopicity. During deep and through impregnation with a colored solution, wood is colored due to the solution moving inside the wood through the cavities of cells having a tubular structure. Having penetrated inside the wood through the capillaries of vessels, tracheids and medullary rays, the dye colors the cell walls, diffusing into their intercapillary spaces. In this case, the cell walls are colored more intensively than the cell cavities. The increase in the strength of modified wood is explained by insufficient water adsorption due to a decrease in the diameter of tracheids filled with the modifier solution; apparently, this is also associated with a decrease in the contact area with water of the glue–wood boundary layer due to a decrease in the size of the cell cavities. The shear strength along the fibers corresponds to the European standard EN205 D4. The increase in water resistance of modified wood is due to the fact that urea compacts the wood and gives it increased dimensional stability.