Abstract <p>Synthetic nanotubes of nickel hydrosilicate (pecoraite) are treated with aqueous solutions of cobalt chloride, sulfate, and nitrate at various temperatures and salt concentrations under hydrothermal conditions. It is shown that under hydrothermal conditions, when nanotubes interact with a 0.1 M solution of cobalt nitrate for more than 4 h at a temperature ≥180°С the formation of the cobalt oxide phase Co<sub>3</sub>O<sub>4</sub> is observed in the form of crystals of lamellar morphology. This phase actively crystallizes with the concentration of the Co(NO<sub>3</sub>)<sub>2</sub> solution increasing up to 0.5 M. At the same time, the nanotubular structure of pecoraite is preserved. In the case of treating nanotubes with solutions of cobalt sulfate and chloride, significant amorphization of the hydrosilicate structure is observed, most likely leading to the complete destruction of the tubular morphology at a temperature of 220°C.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Interaction of Cobalt Salt Solutions and Nickel Hydrosilicate Nanotubes

  • 期刊论文

  • 发表日期：

    2025年4月1日

查看全文
  • I. D. Bystrevskii,
  • E. N. Gatina,
  • V. L. Ugolkov

摘要

Abstract

Synthetic nanotubes of nickel hydrosilicate (pecoraite) are treated with aqueous solutions of cobalt chloride, sulfate, and nitrate at various temperatures and salt concentrations under hydrothermal conditions. It is shown that under hydrothermal conditions, when nanotubes interact with a 0.1 M solution of cobalt nitrate for more than 4 h at a temperature ≥180°С the formation of the cobalt oxide phase Co3O4 is observed in the form of crystals of lamellar morphology. This phase actively crystallizes with the concentration of the Co(NO3)2 solution increasing up to 0.5 M. At the same time, the nanotubular structure of pecoraite is preserved. In the case of treating nanotubes with solutions of cobalt sulfate and chloride, significant amorphization of the hydrosilicate structure is observed, most likely leading to the complete destruction of the tubular morphology at a temperature of 220°C.