Abstract <p>In order to process the low-grade wad clay (Mn 4–6%) which is deposited in the central region of D.P.R of Korea, slurry electro leaching method (diaphragm electrolysis) was applied. The effects of the temperature, current density, ratio of liquid to solid (L/S), time and coagulant agent were observed through the basic experiment on slurry electro leaching of the wad clay. The main condition for the slurry electro leaching was as follows: current density 150–200 A/m<sup>2</sup>, temperature &gt;65°C, L/S = 10 : 1, time 1.1 time of theoretical leaching time and amount of the coagulant agent 50 g/t. Under these conditions, the leaching rate was above 95% and the content of Mn in anodic electrodeposits is 45%. Slime in the wad clay greatly affected the purity of MnO<sub>2</sub> formed on the anode.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

A Study on the Extraction of Manganese from Wad Clay by Slurry Electrolysis

  • 期刊论文

  • 发表日期：

    2025年6月1日

查看全文
  • Jon Yong Nam,
  • Li Hye Song,
  • Kim Chol Jin,
  • Kim Kuk Chol

摘要

Abstract

In order to process the low-grade wad clay (Mn 4–6%) which is deposited in the central region of D.P.R of Korea, slurry electro leaching method (diaphragm electrolysis) was applied. The effects of the temperature, current density, ratio of liquid to solid (L/S), time and coagulant agent were observed through the basic experiment on slurry electro leaching of the wad clay. The main condition for the slurry electro leaching was as follows: current density 150–200 A/m2, temperature >65°C, L/S = 10 : 1, time 1.1 time of theoretical leaching time and amount of the coagulant agent 50 g/t. Under these conditions, the leaching rate was above 95% and the content of Mn in anodic electrodeposits is 45%. Slime in the wad clay greatly affected the purity of MnO2 formed on the anode.