Abstract <p>The concept of “thermal equivalents” of impact damage in composites, created by iteratively fitting the parameters of flat bottom hole defects, has been elaborated. In thin-walled composites, impact damage tends to be located near the surface opposite to the impact, so thermal inspection on the rear surface of the product is most effective for their detection. Detection of defects on the front surface is associated with small signal amplitudes in the region of temperature indications and requires the use of the thermal equivalent of impact damage in the form of a combination of flat bottom hole defects. On the rear surface, temperature indications of impact damage are often butterfly-shaped and characterized by a large area of defect “footprints.” Single flat-bottom flaws can serve as thermal equivalents of such defects. The proposed concept of thermal equivalents of real defects in composites is verified experimentally on a carbon fiber-reinforced plastic specimen with impact damage of 62 J energy.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Modeling and Experimental Study of Thermal Equivalents of Impact Damage in Composites during the Development of Reference Samples in Thermal Testing

  • 期刊论文

  • 发表日期：

    2025年6月1日

查看全文
  • V. P. Vavilov,
  • A. O. Chulkov,
  • O. A. Ganina

摘要

Abstract

The concept of “thermal equivalents” of impact damage in composites, created by iteratively fitting the parameters of flat bottom hole defects, has been elaborated. In thin-walled composites, impact damage tends to be located near the surface opposite to the impact, so thermal inspection on the rear surface of the product is most effective for their detection. Detection of defects on the front surface is associated with small signal amplitudes in the region of temperature indications and requires the use of the thermal equivalent of impact damage in the form of a combination of flat bottom hole defects. On the rear surface, temperature indications of impact damage are often butterfly-shaped and characterized by a large area of defect “footprints.” Single flat-bottom flaws can serve as thermal equivalents of such defects. The proposed concept of thermal equivalents of real defects in composites is verified experimentally on a carbon fiber-reinforced plastic specimen with impact damage of 62 J energy.