Abstract <p>The relationship by mass between phase transformations upon heating and cooling of Ti–55.6% Ni alloy in a state aged in various modes with its shape change during the implementation of a one-way shape memory effect has been studied. It is shown that shape restoration occurs in two stages after deformation at –10°C with 2% bending, In this case, one stage is characterized by a small (0.3–0.4%) restored deformation and the other stage by a large deformation value (1.0–1.1%). A small part of the deformation (0.3–0.4%) is eliminated at the low-temperature stage of shape restoration after two hours of aging at 520°C and two-stage processing at 520 + 460°C and at the high-temperature stage after aging at 460°C. X-ray diffraction tests showed that the duration of the first and second stages of shape change depended on the sequence of occurrence and/or the superposition of R → B2, B19' → R and B19' → B2 transformations during heating.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Change in the Phase Composition of a NiTi-Based Alloy during the Implementation of the Shape Memory Effect

  • 期刊论文

  • 发表日期：

    2025年3月1日

查看全文
  • O. S. Alsaeva,
  • D. E. Gusev,
  • M. Yu. Kollerov,
  • A. O. Snegirev,
  • A. V. Shalin

摘要

Abstract

The relationship by mass between phase transformations upon heating and cooling of Ti–55.6% Ni alloy in a state aged in various modes with its shape change during the implementation of a one-way shape memory effect has been studied. It is shown that shape restoration occurs in two stages after deformation at –10°C with 2% bending, In this case, one stage is characterized by a small (0.3–0.4%) restored deformation and the other stage by a large deformation value (1.0–1.1%). A small part of the deformation (0.3–0.4%) is eliminated at the low-temperature stage of shape restoration after two hours of aging at 520°C and two-stage processing at 520 + 460°C and at the high-temperature stage after aging at 460°C. X-ray diffraction tests showed that the duration of the first and second stages of shape change depended on the sequence of occurrence and/or the superposition of R → B2, B19' → R and B19' → B2 transformations during heating.