Abstract <p>High-temperature oxidation of NH<sub>3</sub> with air to NO oxide on catalytic platinum alloy gauzes is used in the industrial production of nitric acid. Scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDS) with the probe electron energy of 5 and 20 keV were used to characterize chemical composition of the etching structure on Pt(poly) after NH<sub>3</sub> oxidation with air at a pressure of 3.6 bar and 1133 К. Pt, Fe, Si, Al, Mg, O, N and C were detected in the etching structures, which contain oxide particles, crystal platinum pyramids and etch pits (grooves). Pt and О were detected in high concentrations (22.2–69.0 at %), while other elements—in low ones (0.2–8.4 at %). Oxide particles ca. 100 nm in size with the composition MgFe<sub>2</sub>O<sub>4</sub> and a spinel structure are formed from Mg, Fe impurities during NH<sub>3</sub> oxidation. Nucleation and growth of platinum pyramids, etch pits and deep etch grooves proceed during the capture of Pt and PtO<sub>2</sub> from gas phase by MgFe<sub>2</sub>O<sub>4</sub> particles, migration of Pt atoms through the oxide particles to the metal-oxide boundary, and their attachment to the Pt crystal lattice. The formation of etching structure can proceed by the vapor-liquid-solid (VLS) mechanism.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

The Role of Fe and Mg Oxides in the Etching of Polycrystalline Platinum during Catalytic Oxidation of Ammonia with Air at 1133 K

  • 期刊论文

  • 发表日期：

    2025年12月1日

查看全文
  • A. N. Salanov,
  • A. N. Serkova,
  • A. S. Zhirnova,
  • L. A. Isupova,
  • V. N. Parmon

摘要

Abstract

High-temperature oxidation of NH3 with air to NO oxide on catalytic platinum alloy gauzes is used in the industrial production of nitric acid. Scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDS) with the probe electron energy of 5 and 20 keV were used to characterize chemical composition of the etching structure on Pt(poly) after NH3 oxidation with air at a pressure of 3.6 bar and 1133 К. Pt, Fe, Si, Al, Mg, O, N and C were detected in the etching structures, which contain oxide particles, crystal platinum pyramids and etch pits (grooves). Pt and О were detected in high concentrations (22.2–69.0 at %), while other elements—in low ones (0.2–8.4 at %). Oxide particles ca. 100 nm in size with the composition MgFe2O4 and a spinel structure are formed from Mg, Fe impurities during NH3 oxidation. Nucleation and growth of platinum pyramids, etch pits and deep etch grooves proceed during the capture of Pt and PtO2 from gas phase by MgFe2O4 particles, migration of Pt atoms through the oxide particles to the metal-oxide boundary, and their attachment to the Pt crystal lattice. The formation of etching structure can proceed by the vapor-liquid-solid (VLS) mechanism.