<p>Plastic waste represents an escalating environmental challenge and necessitates scalable processing strategies consistent with the United Nations’ Sustainable Development Goal 12 on responsible consumption and production. This work examines controlled hot pressing of polyethylene-based waste as a physical upcycling route for producing functional laminate sheets. Low-density polyethylene (LDPE), high-density polyethylene (HDPE), and polyethylene-coated polypropylene (PP/PE composite) were investigated, with processing temperature, pressure, and dwell time systematically analysed using an orthogonal experimental design. LDPE exhibited the most favourable forming behaviour, achieving continuous sheet formation at 120–130&#xa0;°C under a nominal pressure of approximately 0.59&#xa0;MPa with limited thickness variation. Relative to unprocessed films, hot-pressed materials displayed reduced surface friction and increased water contact angles, indicating decreased surface wettability under the applied conditions. Microscopic observations revealed modified surface morphology after processing, while elemental mapping showed no pronounced changes in macroscopic elemental distribution. HDPE achieved comparable consolidation, whereas PP/PE composites did not form continuous laminates. The results indicate that controlled hot pressing provides a low-energy and reproducible pathway for converting post-consumer polyethylene films into functional materials for circular applications.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Controlled hot pressing for functional upcycling of waste polyethylene materials

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2026年3月4日

查看全文
  • Dong Cheng,
  • Wen-Jie Yan

摘要

Plastic waste represents an escalating environmental challenge and necessitates scalable processing strategies consistent with the United Nations’ Sustainable Development Goal 12 on responsible consumption and production. This work examines controlled hot pressing of polyethylene-based waste as a physical upcycling route for producing functional laminate sheets. Low-density polyethylene (LDPE), high-density polyethylene (HDPE), and polyethylene-coated polypropylene (PP/PE composite) were investigated, with processing temperature, pressure, and dwell time systematically analysed using an orthogonal experimental design. LDPE exhibited the most favourable forming behaviour, achieving continuous sheet formation at 120–130 °C under a nominal pressure of approximately 0.59 MPa with limited thickness variation. Relative to unprocessed films, hot-pressed materials displayed reduced surface friction and increased water contact angles, indicating decreased surface wettability under the applied conditions. Microscopic observations revealed modified surface morphology after processing, while elemental mapping showed no pronounced changes in macroscopic elemental distribution. HDPE achieved comparable consolidation, whereas PP/PE composites did not form continuous laminates. The results indicate that controlled hot pressing provides a low-energy and reproducible pathway for converting post-consumer polyethylene films into functional materials for circular applications.