<p>A new type of green building materials named alkali-activated slag cementitious materials with seawater and sea sand (AASCM-SS) was proposed. AASCM-SS can effectively utilize waste slag, especially suitable for emergency repair projects in coastal areas. To promote its engineering application, the mechanical properties of AASCM-SS at room temperature and high temperature were studied. The influence of polypropylene (PPFs) and polyvinyl alcohol fiber (PVA) on mass loss rate, deformation, compressive strength, flexural strength, and micromorphology of AASCM-SS after high temperature were studied. The research results show that PPFs and PVA can hardly improve the compressive but can slightly improve the flexural strength of AASCM-SS at room temperature. Besides, PPFs and PVA can significantly improve the high temperature resistance of AASCM-SS, with the best effect at temperatures ranging from 200 ~ 400&#xa0;°C. Moreover, adding PPFs and PVA reduced the deformation of AASCM-SS after high temperature. At last, the channels formed after the melting of PPFs and PVA reduced the internal vapor pressure of AASCM-SS, thereby improving its high temperature resistance.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Effect of polypropylene and polyvinyl alcohol fiber on mechanical properties of AASCM-SS after high temperature

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2025年2月20日

查看全文
  • Qingwei Chen,
  • Zhanfei Qu,
  • Liang Yin,
  • Jingjie Liu

摘要

A new type of green building materials named alkali-activated slag cementitious materials with seawater and sea sand (AASCM-SS) was proposed. AASCM-SS can effectively utilize waste slag, especially suitable for emergency repair projects in coastal areas. To promote its engineering application, the mechanical properties of AASCM-SS at room temperature and high temperature were studied. The influence of polypropylene (PPFs) and polyvinyl alcohol fiber (PVA) on mass loss rate, deformation, compressive strength, flexural strength, and micromorphology of AASCM-SS after high temperature were studied. The research results show that PPFs and PVA can hardly improve the compressive but can slightly improve the flexural strength of AASCM-SS at room temperature. Besides, PPFs and PVA can significantly improve the high temperature resistance of AASCM-SS, with the best effect at temperatures ranging from 200 ~ 400 °C. Moreover, adding PPFs and PVA reduced the deformation of AASCM-SS after high temperature. At last, the channels formed after the melting of PPFs and PVA reduced the internal vapor pressure of AASCM-SS, thereby improving its high temperature resistance.