<p>In order to provide long-term anti-corrosion properties of the coatings on the substrate, a microcapsule self-healing coatings system was designed in this paper. Microcapsules were synthesized with ethyl cellulose and octadecyl amine, which were added to epoxy resin to prepare self-healing coatings. The shape of microcapsules was spherical, the average particle size of microcapsules was about 100–120&#xa0;μm, and the average thickness of microcapsules was 4.43&#xa0;μm, which was conducive to the preparation of the coatings. The initial evaporation temperature of the microcapsules was 165℃. The ethyl cellulose organic crosslinked shell enhances the strength of the microcapsules and improves the thermal stability of the microcapsules. Electrochemical impedance spectroscopy showed that the impedance of the coatings with 6 wt% microcapsules was about 2.68 × 10<sup>6</sup> Ω/cm<sup>2</sup>, which was 2 orders of magnitude higher than that of the coatings without microcapsules (5.23 × 10<sup>4</sup>&#xa0;Ω/cm<sup>2</sup>). Scanning electron microscope was used to observe the artificial scratches of the coatings for 24&#xa0;h, and it was found that the microcapsule could repair the artificial scratches of the coatings well. The results showed that the addition of microcapsules can improve the anti-corrosion properties of the coatings.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Properties and corrosion resistance mechanism of a self-healing octadecyl amine loaded ethyl cellulose microcapsule coatings loaded with epoxy resin

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2025年1月9日

查看全文
  • Qidong Cao,
  • Shumei Kang,
  • Chenshuo Lu,
  • Dongpeng Sun,
  • Jinghao Li,
  • Hong Chen,
  • Xintong Li

摘要

In order to provide long-term anti-corrosion properties of the coatings on the substrate, a microcapsule self-healing coatings system was designed in this paper. Microcapsules were synthesized with ethyl cellulose and octadecyl amine, which were added to epoxy resin to prepare self-healing coatings. The shape of microcapsules was spherical, the average particle size of microcapsules was about 100–120 μm, and the average thickness of microcapsules was 4.43 μm, which was conducive to the preparation of the coatings. The initial evaporation temperature of the microcapsules was 165℃. The ethyl cellulose organic crosslinked shell enhances the strength of the microcapsules and improves the thermal stability of the microcapsules. Electrochemical impedance spectroscopy showed that the impedance of the coatings with 6 wt% microcapsules was about 2.68 × 106 Ω/cm2, which was 2 orders of magnitude higher than that of the coatings without microcapsules (5.23 × 104 Ω/cm2). Scanning electron microscope was used to observe the artificial scratches of the coatings for 24 h, and it was found that the microcapsule could repair the artificial scratches of the coatings well. The results showed that the addition of microcapsules can improve the anti-corrosion properties of the coatings.