<p>The utilization of luminescent phosphors in barcode technology can enhance the security feature. Using NaOH as a reducing agent, we have prepared Gd<sub>2</sub>O<sub>3</sub>:Eu<sup>3+</sup>/Er<sup>3+</sup> for luminescent phosphor. The cubic structure of Gd<sub>2</sub>O<sub>3</sub> phosphor is confirmed by the structural analysis conducted using XRD. Dopant Eu and Er induce lattice contraction and expansion in the host lattice, respectively. Based on SEM analysis, porous and irregular particles with an average size of 401&#xa0;nm were observed. In Tem analysis of prepared phosphor have some particle are in spherical in shape. The formation of Gd<sub>2</sub>O<sub>3</sub> was confirmed by Gd-O band stretching as shown in the FTIR analysis. The emission in the red and green regions is emitted by Gd<sub>2</sub>O<sub>3</sub>:Eu<sup>3+</sup> and Gd<sub>2</sub>O<sub>3</sub>:Er<sup>3+</sup>, respectively. The emission peaks of Gd<sub>2</sub>O<sub>3</sub>:Eu<sup>3+</sup>/Er<sup>3+</sup> are observed at 524&#xa0;nm, 539&#xa0;nm, 549&#xa0;nm, 563&#xa0;nm, 593&#xa0;nm, 612&#xa0;nm, and 629&#xa0;nm when it is triggered by 363&#xa0;nm, with a maximum energy transfer efficiency of 95.93%. Enhancing the security of barcodes can be achieved through the use of color-tunable Gd<sub>2</sub>O<sub>3</sub>:Eu<sup>3+</sup>/Er<sup>3+</sup> phosphor. Gd<sub>2</sub>O<sub>3</sub>:Er<sup>3+</sup> (1.5&#xa0;mol%) is a prominent candidate for LED bulbs due to its CCT (5765&#xa0;K).</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Tuning photoluminescence in Gd2O3 via lattice engineering for advanced barcode and LEDs applications

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2025年10月28日

查看全文
  • Praful P. Khode,
  • Merciana N. Sylvester,
  • Nikolay G. Naumov,
  • Anil M. Pethe,
  • S. J. Dhoble

摘要

The utilization of luminescent phosphors in barcode technology can enhance the security feature. Using NaOH as a reducing agent, we have prepared Gd2O3:Eu3+/Er3+ for luminescent phosphor. The cubic structure of Gd2O3 phosphor is confirmed by the structural analysis conducted using XRD. Dopant Eu and Er induce lattice contraction and expansion in the host lattice, respectively. Based on SEM analysis, porous and irregular particles with an average size of 401 nm were observed. In Tem analysis of prepared phosphor have some particle are in spherical in shape. The formation of Gd2O3 was confirmed by Gd-O band stretching as shown in the FTIR analysis. The emission in the red and green regions is emitted by Gd2O3:Eu3+ and Gd2O3:Er3+, respectively. The emission peaks of Gd2O3:Eu3+/Er3+ are observed at 524 nm, 539 nm, 549 nm, 563 nm, 593 nm, 612 nm, and 629 nm when it is triggered by 363 nm, with a maximum energy transfer efficiency of 95.93%. Enhancing the security of barcodes can be achieved through the use of color-tunable Gd2O3:Eu3+/Er3+ phosphor. Gd2O3:Er3+ (1.5 mol%) is a prominent candidate for LED bulbs due to its CCT (5765 K).