<p>In the present study, the magnetic chitosan cross-linked with oxidized chitosan biopolymer was modified with bovine serum albumin protein. Then, the prepared magnetic biosupport was treated with AgNO<sub>3</sub> solution under ultrasonic irradiation. After that Ag decoration on the magnetic BSA-modified chitosan support surface, the obtained Fe<sub>3</sub>O<sub>4</sub>@BSA-CS@Ag/Ag<sub>2</sub>O nanocomposite was characterized by various techniques including FT-IR, FE-SEM, TEM, EDS, XRD, VSM, BET and ICP. This nanocatalyst showed excellent efficiency in the reduction reaction of nitroarenes and organic dyes containing methylene blue, methyl orange, and rhodamine B. The advantages of this catalytic system is high conversion at short reaction times using a small amount of silver-based catalyst, easy separation of the catalyst from the reaction mixture with an external magnet and its reusability in the reduction reaction.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Decoration of silver and silver oxide nanoparticles on a magnetic albumin modified Chitosan support and its catalytic efficiency investigation

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2025年7月12日

查看全文
  • Nazi Salekmokhtari,
  • Fatemeh Rafiee

摘要

In the present study, the magnetic chitosan cross-linked with oxidized chitosan biopolymer was modified with bovine serum albumin protein. Then, the prepared magnetic biosupport was treated with AgNO3 solution under ultrasonic irradiation. After that Ag decoration on the magnetic BSA-modified chitosan support surface, the obtained Fe3O4@BSA-CS@Ag/Ag2O nanocomposite was characterized by various techniques including FT-IR, FE-SEM, TEM, EDS, XRD, VSM, BET and ICP. This nanocatalyst showed excellent efficiency in the reduction reaction of nitroarenes and organic dyes containing methylene blue, methyl orange, and rhodamine B. The advantages of this catalytic system is high conversion at short reaction times using a small amount of silver-based catalyst, easy separation of the catalyst from the reaction mixture with an external magnet and its reusability in the reduction reaction.