<p>Due to human activities such as mining, metal smelting, and sewage irrigation, a significant amount of heavy metals have entered the environment, exacerbating the problem of heavy metal pollution in water bodies. The study of rapid adsorption and removal of lead is particularly critical due to its slow degradation and severe environmental impact. In this study, wheat bran was utilized as an adsorbent and modified using a sodium hydroxide solution. Kinetic and equilibrium adsorption studies were conducted to evaluate the adsorption performance of alkali modified wheat bran on lead ions in water. The adsorption behavior and mechanism of alkali modified wheat bran on Pb<sup>2+</sup> were analyzed from three perspectives: time, concentration, and pH, in conjunction with surface functional groups and microscopic characteristics. The results indicated that the adsorption capacity of alkali modified wheat bran was achieved at pH 4, a concentration of 100&#xa0;mg/L, and an duration of approximately 120&#xa0;min. Experimental data shows that at about 120&#xa0;min, its adsorption efficiency reaches its peak at 81.74%. The fitting results of the adsorption kinetics model and isothermal adsorption model indicate that the adsorption of modified wheat bran is characterized by single-layer chemical adsorption; The alkaline modification treatment increased the porosity of the surface pores of wheat bran, resulting in a rougher surface and an enhanced adsorption area. Furthermore, post-modification, the wheat bran exhibited increased C-H and C = O functional groups, thereby improving the adsorption of Pb<sup>2+</sup>.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Study on the adsorption of Pb2+ in aqueous solution by alkali modified wheat bran

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2025年7月1日

查看全文
  • Jianling Xu,
  • Xinyu Wang,
  • Wenjing Kang,
  • Wenqiu Zhang

摘要

Due to human activities such as mining, metal smelting, and sewage irrigation, a significant amount of heavy metals have entered the environment, exacerbating the problem of heavy metal pollution in water bodies. The study of rapid adsorption and removal of lead is particularly critical due to its slow degradation and severe environmental impact. In this study, wheat bran was utilized as an adsorbent and modified using a sodium hydroxide solution. Kinetic and equilibrium adsorption studies were conducted to evaluate the adsorption performance of alkali modified wheat bran on lead ions in water. The adsorption behavior and mechanism of alkali modified wheat bran on Pb2+ were analyzed from three perspectives: time, concentration, and pH, in conjunction with surface functional groups and microscopic characteristics. The results indicated that the adsorption capacity of alkali modified wheat bran was achieved at pH 4, a concentration of 100 mg/L, and an duration of approximately 120 min. Experimental data shows that at about 120 min, its adsorption efficiency reaches its peak at 81.74%. The fitting results of the adsorption kinetics model and isothermal adsorption model indicate that the adsorption of modified wheat bran is characterized by single-layer chemical adsorption; The alkaline modification treatment increased the porosity of the surface pores of wheat bran, resulting in a rougher surface and an enhanced adsorption area. Furthermore, post-modification, the wheat bran exhibited increased C-H and C = O functional groups, thereby improving the adsorption of Pb2+.