<p>In the process of basic oxygen furnace steelmaking, the high-velocity jet impacts the molten metal pool, resulting in the generation of splashing metal droplets with varying particle sizes. The expansion decarburization of metal droplets in the emulsion phase is one of the main steel-slag reaction behaviors. In this paper, firstly, a theoretical decarburization model of expansion droplet was established, finding biases in their calculation results. Then, the solid phase ratio in different FeO content of slag was analyzed, demonstrating its significant impact on the reactivity performance of slag. Finally, an improved decarburization comprehensive model for expanded droplets, based on the solid phase ratio of slag and data fitting, was developed and validated using experimental data. The results indicate that the improved droplet decarburisation comprehensive model shows a good agreement with the experimental data in predicting changes in carbon content, with Pearson correlation coefficient exceeding 0.94 for different FeO contents. ‌For FeO contents of 3%, 10%, 20%, and 30%, the model achieves MAE (0.035%, 0.024%, 0.056%, 0.059%) and RMSE (0.0034%, 0.0019%, 0.011%, 0.018%), respectively. This model can accurately calculate the change of carbon content of metal droplets under various complex multiphase slag conditions.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Modeling the decarburization of expansion droplets based on the solid phase ratio of slag and data fitting during BOF steelmaking process

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2025年5月10日

查看全文
  • Zi-cheng Xin,
  • Wen-hui Lin,
  • Jiang-shan Zhang,
  • Kai-xiang Peng,
  • Qing Liu

摘要

In the process of basic oxygen furnace steelmaking, the high-velocity jet impacts the molten metal pool, resulting in the generation of splashing metal droplets with varying particle sizes. The expansion decarburization of metal droplets in the emulsion phase is one of the main steel-slag reaction behaviors. In this paper, firstly, a theoretical decarburization model of expansion droplet was established, finding biases in their calculation results. Then, the solid phase ratio in different FeO content of slag was analyzed, demonstrating its significant impact on the reactivity performance of slag. Finally, an improved decarburization comprehensive model for expanded droplets, based on the solid phase ratio of slag and data fitting, was developed and validated using experimental data. The results indicate that the improved droplet decarburisation comprehensive model shows a good agreement with the experimental data in predicting changes in carbon content, with Pearson correlation coefficient exceeding 0.94 for different FeO contents. ‌For FeO contents of 3%, 10%, 20%, and 30%, the model achieves MAE (0.035%, 0.024%, 0.056%, 0.059%) and RMSE (0.0034%, 0.0019%, 0.011%, 0.018%), respectively. This model can accurately calculate the change of carbon content of metal droplets under various complex multiphase slag conditions.