<p>H<sub>2</sub> plasma-enabled reduction of iron ore is a promising green alternative for reducing CO<sub>2</sub> emissions in the iron and steelmaking industry. In this work, we develop an <i>operando</i> plasma transmission electron microscopy (TEM) technique enabling the direct and real-time observation of magnetite (Fe<sub>3</sub>O<sub>4</sub>) nanoparticle reduction by non-thermal H<sub>2</sub> plasma with a spatial resolution of ~1 nm. Our <i>operando</i> results show a decrease in particle size accompanied by crack formation on timescales of ~10 s. We reveal that these observations are due to the oxide reduction, which induces a change in crystal structure from magnetite to iron, driven by the hydrogen radical, H<sup>•</sup>. The <i>operando</i> reduction in particle volume by the plasma is well described by a shrinking-core reaction model. Our findings provide critical insights into mechanisms and rate-controlling processes of non-thermal iron ore reduction at the nanoscale. The developed <i>operando</i> plasma TEM technique is expected to find widespread application with the advent of non-thermal plasma technologies and the growing demands for diagnostic techniques to enhance mechanistic understandings in the field of plasma-nanoengineering.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Revealing the mechanisms of non-thermal plasma-enabled iron oxide reduction through nanoscale operando TEM

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2025年8月14日

查看全文
  • Jae Hyun Nam,
  • K. Andre Mkhoyan,
  • Daan Hein Alsem,
  • Peter J. Bruggeman

摘要

H2 plasma-enabled reduction of iron ore is a promising green alternative for reducing CO2 emissions in the iron and steelmaking industry. In this work, we develop an operando plasma transmission electron microscopy (TEM) technique enabling the direct and real-time observation of magnetite (Fe3O4) nanoparticle reduction by non-thermal H2 plasma with a spatial resolution of ~1 nm. Our operando results show a decrease in particle size accompanied by crack formation on timescales of ~10 s. We reveal that these observations are due to the oxide reduction, which induces a change in crystal structure from magnetite to iron, driven by the hydrogen radical, H•. The operando reduction in particle volume by the plasma is well described by a shrinking-core reaction model. Our findings provide critical insights into mechanisms and rate-controlling processes of non-thermal iron ore reduction at the nanoscale. The developed operando plasma TEM technique is expected to find widespread application with the advent of non-thermal plasma technologies and the growing demands for diagnostic techniques to enhance mechanistic understandings in the field of plasma-nanoengineering.