<p>With the continuous development of high-performance copper alloys in modern industries, it becomes increasingly challenging to further enhance their conductivities. The key bottleneck is the existence of an upper limit on the amount of precipitation, leading to inadequate purification of the copper matrix. Here we demonstrate a phenomenon of significant conductivity enhancement in a Cu-Be alloy through undercooling. It shows that lots of spherical Be-rich clusters can spontaneously form in the deeply undercooled alloy. These clusters survive after subsequent solution treatment and are independent from the normal precipitates during aging, thereby leading to additional purification of the copper matrix. Under peak aging, the electrical conductivity of the undercooled alloy reaches up to 80% International Annealed Cu Standard, which is 30% higher than that of the same component alloy prepared in a conventional way, while its strength remains high. Our study provides an alternative way to address the long-standing strength-conductivity trade-off in copper alloys.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Overcoming the trade-off between conductivity and strength in copper alloys through undercooling

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2025年5月29日

查看全文
  • Bowen Zhang,
  • Pingda Xu,
  • Jinyun Wang,
  • Zhenyu Hong,
  • Weili Wang,
  • Fuping Dai

摘要

With the continuous development of high-performance copper alloys in modern industries, it becomes increasingly challenging to further enhance their conductivities. The key bottleneck is the existence of an upper limit on the amount of precipitation, leading to inadequate purification of the copper matrix. Here we demonstrate a phenomenon of significant conductivity enhancement in a Cu-Be alloy through undercooling. It shows that lots of spherical Be-rich clusters can spontaneously form in the deeply undercooled alloy. These clusters survive after subsequent solution treatment and are independent from the normal precipitates during aging, thereby leading to additional purification of the copper matrix. Under peak aging, the electrical conductivity of the undercooled alloy reaches up to 80% International Annealed Cu Standard, which is 30% higher than that of the same component alloy prepared in a conventional way, while its strength remains high. Our study provides an alternative way to address the long-standing strength-conductivity trade-off in copper alloys.