<p>The precipitation of calcium carbonate (CaCO<sub>3</sub>) polymorphs (calcite, vaterite, and aragonite) plays a crucial role in tailoring the physicochemical properties of construction materials during mineral carbonation. This study systematically explores the influence of pH, temperature, and the [Ca<sup>2+</sup>]: [CO<sub>3</sub><sup>2−</sup>] ratio on the formation, quantitative composition, mineralogy, and morphology of these polymorphs. Results demonstrate that calcite predominates at pH &lt; 7 and &gt; 10, while vaterite forms primarily between pH 7 and 10, with the highest yield (83%) at pH 8.4. Calcite reaches a maximum yield (98%) at pH 12. No aragonite was detected at any pH. Temperature significantly influences the formation of calcium carbonate polymorphs. Calcite and vaterite are primarily formed at temperatures below 50&#xa0;°C. Aragonite begin to appear between 50&#xa0;°C and 85&#xa0;°C, with the highest yield of 96% observed at 80&#xa0;°C. However, at temperatures above 90&#xa0;°C, aragonite gradually transforms into calcite. A higher [Ca<sup>2+</sup>]: [CO<sub>3</sub><sup>2−</sup>] ratio favors calcite formation. Morphological analysis using FE-SEM reveals spherical vaterite, rhombohedral calcite, and needle-like aragonite. A nanoscale calcite (&lt; 200&#xa0;nm) with rhomboidal shapes formed at pH 12.5. TGA confirms that vaterite and aragonite are thermodynamically less stable, eventually converting to calcite, attributed to the higher coordination numbers and ligand-ligand repulsion in [CaO<sub>12</sub>] (vaterite) and [CaO<sub>9</sub>] (aragonite) versus [CaO<sub>6</sub>] (calcite).</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Effects of temperature, pH and calcium-to-carbonate ratio on the calcium carbonate polymorphs

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2025年8月15日

查看全文
  • Mohd Hanifa,
  • Usha Sharma,
  • P. C. Thapliyal,
  • L. P. Singh

摘要

The precipitation of calcium carbonate (CaCO3) polymorphs (calcite, vaterite, and aragonite) plays a crucial role in tailoring the physicochemical properties of construction materials during mineral carbonation. This study systematically explores the influence of pH, temperature, and the [Ca2+]: [CO32−] ratio on the formation, quantitative composition, mineralogy, and morphology of these polymorphs. Results demonstrate that calcite predominates at pH < 7 and > 10, while vaterite forms primarily between pH 7 and 10, with the highest yield (83%) at pH 8.4. Calcite reaches a maximum yield (98%) at pH 12. No aragonite was detected at any pH. Temperature significantly influences the formation of calcium carbonate polymorphs. Calcite and vaterite are primarily formed at temperatures below 50 °C. Aragonite begin to appear between 50 °C and 85 °C, with the highest yield of 96% observed at 80 °C. However, at temperatures above 90 °C, aragonite gradually transforms into calcite. A higher [Ca2+]: [CO32−] ratio favors calcite formation. Morphological analysis using FE-SEM reveals spherical vaterite, rhombohedral calcite, and needle-like aragonite. A nanoscale calcite (< 200 nm) with rhomboidal shapes formed at pH 12.5. TGA confirms that vaterite and aragonite are thermodynamically less stable, eventually converting to calcite, attributed to the higher coordination numbers and ligand-ligand repulsion in [CaO12] (vaterite) and [CaO9] (aragonite) versus [CaO6] (calcite).