<p>In the present work, comprehensive structural and magnetic studies of the vacuum- and air-annealed, followed by rapid quenching Fe<sub>85.3</sub>Cu<sub>0.7</sub>B<sub>14</sub> ribbons, modified by Co and Mo, have been reported. Three different alloys, i.e. Fe<sub>80.3</sub>Co<sub>5</sub>Cu<sub>0.7</sub>B<sub>14</sub>, Fe<sub>80.3</sub>Mo<sub>5</sub>Cu<sub>0.7</sub>B<sub>14</sub>, and Fe<sub>75.3</sub>Co<sub>5</sub>Mo<sub>5</sub>Cu<sub>0.7</sub>B<sub>14</sub>, were first produced in the pure amorphous state via melt-spinning technique and then characterised by X-ray diffraction and differential scanning calorimetry methods. Based on these results, the annealing process has been optimised in the temperature range between 280 and 540&#xa0;°C towards improving the magnetic properties (saturation induction (Bs), coercivity (Hc), core power losses at 1&#xa0;T and 50&#xa0;Hz (<i>P</i><sub>10/50</sub>)). For the optimal conditions (at the minimum value of <i>P</i><sub>10/50</sub>), the complex permeability in the 10<sup>4</sup>–10<sup>8</sup>&#xa0;Hz frequency range, together with the core power losses obtained from magnetic induction dependence up to the frequency of 400&#xa0;kHz, was successfully measured. The local and average crystal structures were investigated by the X-ray and neutron diffraction complemented by transmission electron microscopy observations proving for Fe<sub>80.3</sub>Co<sub>5</sub>Cu<sub>0.7</sub>B<sub>14</sub> alloy, the nanocrystalline phase embedded in the glassy matrix, however with the crystal growth rate restricted to only an early stage of crystallisation. In addition, better magnetic parameters of Fe<sub>80.3</sub>Co<sub>5</sub>Cu<sub>0.7</sub>B<sub>14</sub> alloy were obtained for optimal air-annealing conditions than those of the vacuum-annealed sample. The chemical composition mapping along the air-annealed ribbon cross-section indicated an oxygen-rich layer with a thickness of about 140&#xa0;nm. As shown, oxygenation has a positive impact on magnetic properties. Finally, the vacuum- and air-annealed alloys have been characterised using <sup>57</sup>Fe Mössbauer spectrometry and transmission electron microscopy.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Structure and magnetic properties of vacuum- and air-annealed rapidly quenched Mo- and Co-modified Fe85.3Cu0.7B14 alloy

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2025年6月3日

查看全文
  • Lukasz Hawelek,
  • Przemyslaw Zackiewicz,
  • Mariola Kadziolka-Gawel,
  • Anna Wojcik,
  • Wojciech Maziarz,
  • Robert Chulist,
  • Margit Fábián,
  • Tymon Warski

摘要

In the present work, comprehensive structural and magnetic studies of the vacuum- and air-annealed, followed by rapid quenching Fe85.3Cu0.7B14 ribbons, modified by Co and Mo, have been reported. Three different alloys, i.e. Fe80.3Co5Cu0.7B14, Fe80.3Mo5Cu0.7B14, and Fe75.3Co5Mo5Cu0.7B14, were first produced in the pure amorphous state via melt-spinning technique and then characterised by X-ray diffraction and differential scanning calorimetry methods. Based on these results, the annealing process has been optimised in the temperature range between 280 and 540 °C towards improving the magnetic properties (saturation induction (Bs), coercivity (Hc), core power losses at 1 T and 50 Hz (P10/50)). For the optimal conditions (at the minimum value of P10/50), the complex permeability in the 104–108 Hz frequency range, together with the core power losses obtained from magnetic induction dependence up to the frequency of 400 kHz, was successfully measured. The local and average crystal structures were investigated by the X-ray and neutron diffraction complemented by transmission electron microscopy observations proving for Fe80.3Co5Cu0.7B14 alloy, the nanocrystalline phase embedded in the glassy matrix, however with the crystal growth rate restricted to only an early stage of crystallisation. In addition, better magnetic parameters of Fe80.3Co5Cu0.7B14 alloy were obtained for optimal air-annealing conditions than those of the vacuum-annealed sample. The chemical composition mapping along the air-annealed ribbon cross-section indicated an oxygen-rich layer with a thickness of about 140 nm. As shown, oxygenation has a positive impact on magnetic properties. Finally, the vacuum- and air-annealed alloys have been characterised using 57Fe Mössbauer spectrometry and transmission electron microscopy.