<p>The ingenuity of the work lies in joining of 6.18&#xa0;mm thick IN625 plate with single-pass plasma arc welding without any weld groove preparation and without any filler wire. Two welding speeds (100, 120&#xa0;mm/min) and welding currents ranging from 115 to 145 A at 5 A intervals were used. The weld joint metallurgy was characterised using field emission scanning electron microscopy, energy-dispersive X-ray spectroscopy, etc., to establish a connection with the mechanical performance. The micrograph of the fusion zone exhibited a variety of dendritic structures in terms of size and shape, leading to non-uniform true strains across the weld cross-section. The specimen with the smallest fusion zone area attained a maximum joint strength of 831.8 <InlineEquation ID="IEq1"> <InlineMediaObject> <ImageObject Color="BlackWhite" FileRef="43452_2025_1157_Article_IEq1.gif" Format="GIF" Height="13" Rendition="HTML" Resolution="72" Type="Linedraw" Width="19" /> </InlineMediaObject> <EquationSource Format="TEX">\(\pm\)</EquationSource> <EquationSource Format="MATHML"><math> <mo>±</mo> </math></EquationSource> </InlineEquation> 12&#xa0;MPa, which is 96% of the BM strength. The Laves phase formation and the interdendritic microsegregation were particularly noticeable within the fusion zone and contributed to the joint strength reduction. The fusion zone exhibited the lowest microhardness compared to other zones due to the supersaturation of strengthening elements, namely Nb and Mo in the γ-matrix along with Laves phase developed within the weldment. The partition coefficients in the dendritic core of the Nb and Mo elements were less than the one that leads to microsegregation in the interdendritic region. The fracture surface cross-section view showed that the micro-cracks were initiated during the tensile deformation process in the Laves phase. The fracture surface consisted of shallow dimples, which were attributed to low ductile features.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Study of mechanical behaviour and microsegregation in interdendritic region of a single-pass plasma arc welding of thick IN625 plate

  • 期刊论文

  • 发表日期：

    2025年2月1日

查看全文
  • Dipankar Saha,
  • Sukhomay Pal

摘要

The ingenuity of the work lies in joining of 6.18 mm thick IN625 plate with single-pass plasma arc welding without any weld groove preparation and without any filler wire. Two welding speeds (100, 120 mm/min) and welding currents ranging from 115 to 145 A at 5 A intervals were used. The weld joint metallurgy was characterised using field emission scanning electron microscopy, energy-dispersive X-ray spectroscopy, etc., to establish a connection with the mechanical performance. The micrograph of the fusion zone exhibited a variety of dendritic structures in terms of size and shape, leading to non-uniform true strains across the weld cross-section. The specimen with the smallest fusion zone area attained a maximum joint strength of 831.8 \(\pm\) ± 12 MPa, which is 96% of the BM strength. The Laves phase formation and the interdendritic microsegregation were particularly noticeable within the fusion zone and contributed to the joint strength reduction. The fusion zone exhibited the lowest microhardness compared to other zones due to the supersaturation of strengthening elements, namely Nb and Mo in the γ-matrix along with Laves phase developed within the weldment. The partition coefficients in the dendritic core of the Nb and Mo elements were less than the one that leads to microsegregation in the interdendritic region. The fracture surface cross-section view showed that the micro-cracks were initiated during the tensile deformation process in the Laves phase. The fracture surface consisted of shallow dimples, which were attributed to low ductile features.