<p>Medium- and low-temperature coal tar pitch can be prepared as coal-based mesophase pitch for its high value-added utilization. However, its lower aromaticity and higher content of heteroatoms (especially O atoms) led to a higher content of the resulting mesophase pitch mosaic structure. In this study, mesophase pitch was prepared by co-carbonization of high aromaticity, low oxygen content high-temperature refined pitch (RHCTP) with medium- and low-temperature coal tar refined pitch (RCTP). The impact of various blending ratios on the optical and microcrystalline structures of mesophase pitch was analyzed using polarized light microscopy, X-ray diffraction, and Raman spectroscopy. The addition of RHCTP to modify RCTP significantly enhanced the optical and microcrystalline structures of the co-carbonized products. The optimal blending ratio (R-25%) was obtained. Needle coke prepared from mesophase pitch obtained from R-25% had superior fine fiber structure, lowest average resistivity (157.37&#xa0;μΩ·m) and high true density (2.125&#xa0;g/cm<sup>3</sup>). The thermal conversion behavior of the blended refined pitch during co-carbonation was analyzed using thermogravimetric data of the R-25% sample through four isoconversion methods. The thermal conversion of the R-25% sample occurs in three stages: the first stage follows the Parabola law model, while the second and third stages adhere to the random nucleation and nuclei growth model. This analysis of thermal conversion kinetics offers theoretical insights for optimizing mesophase pitch preparation process conditions and reactor design.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Study on co-carbonization characteristics and thermal conversion kinetics of medium- and low-temperature and high-temperature refined pitch

  • 期刊论文

  • 发表日期：

    2025年10月4日

查看全文
  • Shiquan He,
  • Louwei Cui,
  • Jiaojiao Liu,
  • Sijie Wang,
  • Yanyan Song,
  • Ting He,
  • Tao Liu,
  • Huaan Zheng,
  • Yonghong Zhu,
  • Dong Li

摘要

Medium- and low-temperature coal tar pitch can be prepared as coal-based mesophase pitch for its high value-added utilization. However, its lower aromaticity and higher content of heteroatoms (especially O atoms) led to a higher content of the resulting mesophase pitch mosaic structure. In this study, mesophase pitch was prepared by co-carbonization of high aromaticity, low oxygen content high-temperature refined pitch (RHCTP) with medium- and low-temperature coal tar refined pitch (RCTP). The impact of various blending ratios on the optical and microcrystalline structures of mesophase pitch was analyzed using polarized light microscopy, X-ray diffraction, and Raman spectroscopy. The addition of RHCTP to modify RCTP significantly enhanced the optical and microcrystalline structures of the co-carbonized products. The optimal blending ratio (R-25%) was obtained. Needle coke prepared from mesophase pitch obtained from R-25% had superior fine fiber structure, lowest average resistivity (157.37 μΩ·m) and high true density (2.125 g/cm3). The thermal conversion behavior of the blended refined pitch during co-carbonation was analyzed using thermogravimetric data of the R-25% sample through four isoconversion methods. The thermal conversion of the R-25% sample occurs in three stages: the first stage follows the Parabola law model, while the second and third stages adhere to the random nucleation and nuclei growth model. This analysis of thermal conversion kinetics offers theoretical insights for optimizing mesophase pitch preparation process conditions and reactor design.