<p>In this study, near-infrared (NIR) spectroscopy, a measurement method not widely used in dentistry, was used to monitor the synthesis of calcium phosphate cement. Tetra calcium phosphate and di calcium phosphate dihydrate were mixed at a Ca/P ratio of 1.67, and water was added dropwise to induce the phase transition to HAp. The reaction conditions were evaluated by measuring NIR spectra every minute for 60&#xa0;min and every 20&#xa0;min for 24&#xa0;h. The obtained NIR spectra were analyzed using singular value decomposition. The synthesized apatite was characterized by measuring XRD, FT-IR, and SEM. In the self-setting apatite cement system, 24-hour monitoring revealed that a phase transition was achieved. NIR monitoring was found to be effective and valuable for evaluating calcium phosphate cements.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Monitoring of self-setting apatite cement using near-infrared spectroscopy: time-course evaluation using machine learning

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2025年1月24日

查看全文
  • Yuta Otsuka,
  • Sayaka Ito,
  • Kazuyuki Noguchi,
  • Hiroshi Kono,
  • Masafumi Kikuchi

摘要

In this study, near-infrared (NIR) spectroscopy, a measurement method not widely used in dentistry, was used to monitor the synthesis of calcium phosphate cement. Tetra calcium phosphate and di calcium phosphate dihydrate were mixed at a Ca/P ratio of 1.67, and water was added dropwise to induce the phase transition to HAp. The reaction conditions were evaluated by measuring NIR spectra every minute for 60 min and every 20 min for 24 h. The obtained NIR spectra were analyzed using singular value decomposition. The synthesized apatite was characterized by measuring XRD, FT-IR, and SEM. In the self-setting apatite cement system, 24-hour monitoring revealed that a phase transition was achieved. NIR monitoring was found to be effective and valuable for evaluating calcium phosphate cements.