<p>In this study, Al-<i>x</i>Si-0.3Mn-0.3Mg-0.14Fe alloys (<i>x</i>=6.5, 7.5, 8.5, wt.%) were prepared by super-slow-speed die-casting, and the effect of Si content on the microstructure, mechanical and thermal/ electrical conductivities in as-cast, T5, and T6 states (DIN EN 1706:2020) were investigated. It is found that the increase of Si content in the alloy enhances the formation of eutectic segregation band in the casting surface microstructure. Within the Si content range of 6.5%–8.5%, as a comprehensive evaluation criterion of mechanical properties, the quality index (QI) of 376.1 MPa can be obtained in the as-cast state of the alloy with about 7.5% Si content, 373.4 MPa in T5 state of the alloy with 6.5% Si content, and 432.2 MPa in T6 state of the alloy containing 8.5% Si. The heat treatment state significantly affects the thermal conductivity and electrical conductivity of the alloys. The eutectic silicon in the alloy is segemented and further spheroidizaed during the solution process, and the solute atoms of Mg and Si are more adequately precipitated during the aging process. Both of these greatly reduces the probability of electron scattering. Thus, T6 treatment significantly improves the electrical and thermal conductivity. With the increase of Si content, both thermal conductivity and electrical conductivity decrease slightly, demonstrating a strong correlation with the Si content in the alloy.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Effect of Si content on microstructure, mechanical, and thermal/electrical conductivities of Al-xSi-0.3Mn-0.3Mg-0.14Fe alloy prepared by super-slow-speed die-casting

  • 期刊论文

  • 发表日期：

    2025年4月12日

查看全文
  • Lu Zhang,
  • Heng-cheng Liao,
  • Jiang Li

摘要

In this study, Al-xSi-0.3Mn-0.3Mg-0.14Fe alloys (x=6.5, 7.5, 8.5, wt.%) were prepared by super-slow-speed die-casting, and the effect of Si content on the microstructure, mechanical and thermal/ electrical conductivities in as-cast, T5, and T6 states (DIN EN 1706:2020) were investigated. It is found that the increase of Si content in the alloy enhances the formation of eutectic segregation band in the casting surface microstructure. Within the Si content range of 6.5%–8.5%, as a comprehensive evaluation criterion of mechanical properties, the quality index (QI) of 376.1 MPa can be obtained in the as-cast state of the alloy with about 7.5% Si content, 373.4 MPa in T5 state of the alloy with 6.5% Si content, and 432.2 MPa in T6 state of the alloy containing 8.5% Si. The heat treatment state significantly affects the thermal conductivity and electrical conductivity of the alloys. The eutectic silicon in the alloy is segemented and further spheroidizaed during the solution process, and the solute atoms of Mg and Si are more adequately precipitated during the aging process. Both of these greatly reduces the probability of electron scattering. Thus, T6 treatment significantly improves the electrical and thermal conductivity. With the increase of Si content, both thermal conductivity and electrical conductivity decrease slightly, demonstrating a strong correlation with the Si content in the alloy.