<p>Given the economic, industrial, and environmental value of green dihydrogen (H<sub>2</sub>), optimization of water electrolysis as a means of producing H<sub>2</sub> is essential. Binders are a crucial component of electrocatalysts, yet they remain largely underdeveloped, with a significant lack of standardization in the field. Therefore, targeted research into the development of alternative binder systems is essential for advancing performance and consistency. Binders essentially act as the key to regulating the electrode (support)–catalyst–electrolyte interfacial junctions and contribute to the overall reactivity of the electrocatalyst assembly. Therefore, alternative binders were explored with a focus on cost efficiency and environmental compatibility, striving to achieve desirable activity and stability. Herein, the alkaline hydrogen evolution reaction (HER) was investigated, and the sluggish water dissociation step was targeted. Controlled hydrophilic poly(vinyl alcohol)-based hydrogel binders were designed for this application. Three hydrogel binders were evaluated without incorporated electrocatalysts, namely PVA<sub>145</sub>, PVA<sub>145</sub>-<i>blend</i>-bPEI<sub>1.8</sub>, and PVA<sub>145</sub>-<i>blend</i>-PPy. Interestingly, the study revealed that the hydrophilicity of the binders exhibited an enhancing effect on the observed activity, resulting in improved performance compared to the commercial binder, Nafion™. Notably, the PVA<sub>145</sub> system stands out, with an overpotential of 224&#xa0;mV at − 10&#xa0;mA·cm<sup>−2</sup> (geometric) in 1.0&#xa0;M KOH, compared to the 238&#xa0;mV exhibited by Nafion™. Inclusion of Pt as active material in PVA<sub>145</sub> as binder exhibited a synergistic increase in performance, achieving a mass activity of 1.174 A.cm<sup>−2</sup>.mg<sup>−1</sup><sub>Pt</sub> in comparison to Nafion™’s 0.344 A.cm<sup>−2</sup>.mg<sup>−1</sup><sub>Pt</sub>, measured at − 150&#xa0;mV vs RHE. Our research aimed to contribute to the development of cost-effective and efficient binder systems, stressing the necessity to challenge the dominance of the commercially available binders.</p> Graphical Abstract <p></p> <p>Utilization of PVA-based polymers as alternative binders to enhance the sustainability and efficiency of the alkaline HER</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

A Comparative Study of Alternative Polymer Binders for the Hydrogen Evolution Reaction

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2025年8月20日

查看全文
  • Wilhelm Heinrich le Roux,
  • Rueben Pfukwa,
  • Jan Josef Weigand,
  • Anzel Falch

摘要

Given the economic, industrial, and environmental value of green dihydrogen (H2), optimization of water electrolysis as a means of producing H2 is essential. Binders are a crucial component of electrocatalysts, yet they remain largely underdeveloped, with a significant lack of standardization in the field. Therefore, targeted research into the development of alternative binder systems is essential for advancing performance and consistency. Binders essentially act as the key to regulating the electrode (support)–catalyst–electrolyte interfacial junctions and contribute to the overall reactivity of the electrocatalyst assembly. Therefore, alternative binders were explored with a focus on cost efficiency and environmental compatibility, striving to achieve desirable activity and stability. Herein, the alkaline hydrogen evolution reaction (HER) was investigated, and the sluggish water dissociation step was targeted. Controlled hydrophilic poly(vinyl alcohol)-based hydrogel binders were designed for this application. Three hydrogel binders were evaluated without incorporated electrocatalysts, namely PVA145, PVA145-blend-bPEI1.8, and PVA145-blend-PPy. Interestingly, the study revealed that the hydrophilicity of the binders exhibited an enhancing effect on the observed activity, resulting in improved performance compared to the commercial binder, Nafion™. Notably, the PVA145 system stands out, with an overpotential of 224 mV at − 10 mA·cm−2 (geometric) in 1.0 M KOH, compared to the 238 mV exhibited by Nafion™. Inclusion of Pt as active material in PVA145 as binder exhibited a synergistic increase in performance, achieving a mass activity of 1.174 A.cm−2.mg−1Pt in comparison to Nafion™’s 0.344 A.cm−2.mg−1Pt, measured at − 150 mV vs RHE. Our research aimed to contribute to the development of cost-effective and efficient binder systems, stressing the necessity to challenge the dominance of the commercially available binders.

Graphical Abstract

Utilization of PVA-based polymers as alternative binders to enhance the sustainability and efficiency of the alkaline HER