<p>The microstructural characteristics of austenite in Ti microalloyed steel during continuous casting significantly influence the thermoplasticity, thereby affecting the quality of the slab. In this work, a prediction model for two-stage austenite growth under varying cooling rates was established by incorporating the effect of second-phase pinning and high-temperature ferrite–austenite phase transformation and growth theory. The results indicate that with 0.02wt% Ti, the high-temperature ferrite growth exhibits typical parabolic growth characteristics. When the Ti content increases to 0.04wt%, the high-temperature ferrite grain boundary migration rate significantly slows during the initial solidification stage. The predicted austenite grain sizes for 0.02wt% Ti microalloyed steel at the center, quarter, and surface of the slab are 5592, 3529, and 1524 µm, respectively. For 0.04wt% Ti microalloyed steel, the austenite grain sizes are 4074, 2942, and 1179 µm at the same positions. The average error is within 5%. As the Ti content increases from 0.02wt% to 0.04wt%, the austenite grain refinement at the center is most significant, with an average grain size reduction of 27.14%.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Grain growth kinetics model of high-temperature ferrite and austenite in Ti microalloyed steel during continuous casting

  • 期刊论文

  • 发表日期：

    2025年5月26日

查看全文
  • Tianci Chen,
  • Cheng Ji,
  • Jianhua Yang,
  • Yunguang Chi,
  • Miaoyong Zhu

摘要

The microstructural characteristics of austenite in Ti microalloyed steel during continuous casting significantly influence the thermoplasticity, thereby affecting the quality of the slab. In this work, a prediction model for two-stage austenite growth under varying cooling rates was established by incorporating the effect of second-phase pinning and high-temperature ferrite–austenite phase transformation and growth theory. The results indicate that with 0.02wt% Ti, the high-temperature ferrite growth exhibits typical parabolic growth characteristics. When the Ti content increases to 0.04wt%, the high-temperature ferrite grain boundary migration rate significantly slows during the initial solidification stage. The predicted austenite grain sizes for 0.02wt% Ti microalloyed steel at the center, quarter, and surface of the slab are 5592, 3529, and 1524 µm, respectively. For 0.04wt% Ti microalloyed steel, the austenite grain sizes are 4074, 2942, and 1179 µm at the same positions. The average error is within 5%. As the Ti content increases from 0.02wt% to 0.04wt%, the austenite grain refinement at the center is most significant, with an average grain size reduction of 27.14%.