<p>Several classes of materials are being proposed for use in fusion reactors including oxide dispersion strengthened (ODS) and reduced activation ferritic-martensitic (RAF/M) steels to withstand the severe and harsh conditions. In this work, the mechanical properties of a Fe-16Cr-4Al-2W-0.3Ti-0.3Y<sub>2</sub>O<sub>3</sub> (K3) (ODS) ferritic steel and a Fe-8.9Cr-1.1W-0.47Mn-0.2V-0.14Ta-0.11C (Eurofer 97) (RAF/M) steel) after triple ion beam irradiation were locally evaluated utilizing in-situ micro-pillar compression tests, and continuous stiffness/quasi-static nanoindentation. No change in mechanical properties was observed in the K3 ODS steel. However, the Eurofer 97 RAF/M steel exhibited radiation-induced effects via increases in yield strength. Micro-pillar techniques were expanded to neutron-irradiated materials via an in-situ testing technique employing lift-out methods on Fe-14Cr-0.9Ti-0.3Mo-0.25Y<sub>2</sub>O<sub>3</sub> (MA957) ODS ferritic steel. Both the non-irradiated and irradiated compressive yield stresses of the MA 957 micro-pillars were in good agreement with bulk yield stress values reported in the literature, suggesting that the lift-out micro-pillar compression testing technique is a promising method. The demonstration of these techniques on ion beam and neutron irradiated ODS steels and ion beam RAF/M steels gives information to inform models of the material degradation during use in a fusion device.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Comparative Mechanical Properties Analysis of Triple Ion-Beam Irradiated and Neutron Irradiated Potential Plasma Facing Components

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2025年3月3日

查看全文
  • C. Howard,
  • D. Frazer,
  • B. William Choi,
  • A. Lupinacci,
  • S. S. Parker,
  • L. Hsiung,
  • A. Kimura,
  • M. J. Fluss,
  • P. Hosemann

摘要

Several classes of materials are being proposed for use in fusion reactors including oxide dispersion strengthened (ODS) and reduced activation ferritic-martensitic (RAF/M) steels to withstand the severe and harsh conditions. In this work, the mechanical properties of a Fe-16Cr-4Al-2W-0.3Ti-0.3Y2O3 (K3) (ODS) ferritic steel and a Fe-8.9Cr-1.1W-0.47Mn-0.2V-0.14Ta-0.11C (Eurofer 97) (RAF/M) steel) after triple ion beam irradiation were locally evaluated utilizing in-situ micro-pillar compression tests, and continuous stiffness/quasi-static nanoindentation. No change in mechanical properties was observed in the K3 ODS steel. However, the Eurofer 97 RAF/M steel exhibited radiation-induced effects via increases in yield strength. Micro-pillar techniques were expanded to neutron-irradiated materials via an in-situ testing technique employing lift-out methods on Fe-14Cr-0.9Ti-0.3Mo-0.25Y2O3 (MA957) ODS ferritic steel. Both the non-irradiated and irradiated compressive yield stresses of the MA 957 micro-pillars were in good agreement with bulk yield stress values reported in the literature, suggesting that the lift-out micro-pillar compression testing technique is a promising method. The demonstration of these techniques on ion beam and neutron irradiated ODS steels and ion beam RAF/M steels gives information to inform models of the material degradation during use in a fusion device.