<p>The research demonstrated that laser powder bed fusion (LPBF) coupled with controlled annealing at 1200 °C, could significantly increase the proportion of coincidence site lattice (CSL) grain boundary, thereby achieving an outstanding synergy of enhanced strength and exceptional ductility. The plastic deformation behavior, strain hardening behavior, and fracture behavior of LPBF 316L steel annealing at 1200 °C for 20 h were studied through quasi-in-situ tensile process. It was found that LPBF 316L steel formed a certain proportion of deformation twins during the tensile process, and the formation of twins changed the crystal orientation, thus promoting further slip and crystal deformation. The synergistic effect of slip and twin promoted higher plasticity. LPBF process coupled with controlled annealing at 1200 °C for 20 h leads to a ultimate tensile strength of 613 MPa and total elongation of 73.8%.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

High-temperature stability and mechanical property optimization of laser powder bed fusion 316L steel after controlled annealing

  • 期刊论文

  • 发表日期：

    2025年4月1日

查看全文
  • Wen-qi Li,
  • Li-xin Meng,
  • Qian-fen Zhang,
  • Hui-hu Lu,
  • Xiao-feng Niu,
  • Hua Hou

摘要

The research demonstrated that laser powder bed fusion (LPBF) coupled with controlled annealing at 1200 °C, could significantly increase the proportion of coincidence site lattice (CSL) grain boundary, thereby achieving an outstanding synergy of enhanced strength and exceptional ductility. The plastic deformation behavior, strain hardening behavior, and fracture behavior of LPBF 316L steel annealing at 1200 °C for 20 h were studied through quasi-in-situ tensile process. It was found that LPBF 316L steel formed a certain proportion of deformation twins during the tensile process, and the formation of twins changed the crystal orientation, thus promoting further slip and crystal deformation. The synergistic effect of slip and twin promoted higher plasticity. LPBF process coupled with controlled annealing at 1200 °C for 20 h leads to a ultimate tensile strength of 613 MPa and total elongation of 73.8%.