<p>The electrochemical properties of spinel oxide-spinel oxide composites [NiCo<sub>2</sub>O<sub>4</sub>-Mn<sub>1-x</sub>Cr<sub>x</sub>Co<sub>2</sub>O<sub>4</sub> (x = 0.2, 0.6, 0.8)] with regard to oxygen evolution reaction (OER) and methanol oxidation reaction (MOR) have been investigated. Co-precipitation and sol–gel techniques were utilized to synthesize the materials. Fourier-transform infrared (FTIR) spectroscopy, X-Ray Diffraction (XRD) and Scanning Electron Microscopy (SEM) were employed to analyse the physicochemical properties of the synthesized materials. Electrochemical examinations such as cyclic voltammetry (CV) and Tafel experiment were performed in 1&#xa0;M KOH with and without methanol at 25&#xa0;°C. The electrocatalytic performance of the materials was assessed via anodic polarization curves and NiCo<sub>2</sub>O<sub>4</sub>-Mn<sub>0.2</sub>Cr<sub>0.8</sub>Co<sub>2</sub>O<sub>4</sub> was found to be most active towards the OER (j = 33.5 mAcm<sup>−2</sup>) and NiCo<sub>2</sub>O<sub>4</sub>-Mn<sub>0.8</sub>Cr<sub>0.2</sub>Co<sub>2</sub>O<sub>4</sub> was found to be most active towards the MOR (j = 74.3 mAcm<sup>−2</sup>) at 750&#xa0;mV. The electrodes’ durability was investigated using chronoamperometric studies and electrochemically active surface area (ECSA) evaluations using Electrochemical Impedance Spectroscopy (EIS) offered further understanding into the enhancement in electrocatalytic activity. From the EIS experiment, the roughness factor for NiCo<sub>2</sub>O<sub>4</sub>-Mn<sub>0.8</sub>Cr<sub>0.2</sub>Co<sub>2</sub>O<sub>4</sub> and NiCo<sub>2</sub>O<sub>4</sub>-Mn<sub>0.2</sub>Cr<sub>0.8</sub>Co<sub>2</sub>O<sub>4</sub> was calculated and found to be 6.48 &amp; 22.48, respectively in 1&#xa0;M KOH. Using chronoamperometry experiment, the retained current (%) for NiCo<sub>2</sub>O<sub>4</sub>-Mn<sub>0.8</sub>Cr<sub>0.2</sub>Co<sub>2</sub>O<sub>4</sub> and NiCo<sub>2</sub>O<sub>4</sub>-Mn<sub>0.2</sub>Cr<sub>0.8</sub>Co<sub>2</sub>O<sub>4</sub> was found to be 27% and 41%, respectively in 1&#xa0;M KOH. The interplay in the thermodynamic properties of the electrocatalyst has been also investigated for OER and MOR. It was found that the nanocomposite NiCo<sub>2</sub>O<sub>4</sub>-Mn<sub>0.8</sub>Cr<sub>0.2</sub>Co<sub>2</sub>O<sub>4</sub> is well optimized to demand only 35&#xa0;kJ&#xa0;mol<sup>−1</sup> of <InlineEquation ID="IEq1"> <InlineMediaObject> <ImageObject Color="BlackWhite" FileRef="11581_2025_6148_Article_IEq1.gif" Format="GIF" Height="24" Rendition="HTML" Resolution="72" Type="Linedraw" Width="46" /> </InlineMediaObject> <EquationSource Format="TEX">\(\Delta H_{el}^{\circ\#}\)</EquationSource> <EquationSource Format="MATHML"><math> <mrow> <mi mathvariant="normal">Δ</mi> <msubsup> <mi>H</mi> <mrow> <mi mathvariant="italic">el</mi> </mrow> <mrow> <mo>∘</mo> <mo>#</mo> </mrow> </msubsup> </mrow> </math></EquationSource> </InlineEquation> at 650&#xa0;mV for OER and the nanocomposite NiCo<sub>2</sub>O<sub>4</sub>-Mn<sub>0.6</sub>Cr<sub>0.4</sub>Co<sub>2</sub>O<sub>4</sub> demands only 45&#xa0;kJ&#xa0;mol<sup>−1</sup> of <InlineEquation ID="IEq2"> <InlineMediaObject> <ImageObject Color="BlackWhite" FileRef="11581_2025_6148_Article_IEq2.gif" Format="GIF" Height="24" Rendition="HTML" Resolution="72" Type="Linedraw" Width="46" /> </InlineMediaObject> <EquationSource Format="TEX">\(\Delta H_{el}^{\circ\#}\)</EquationSource> <EquationSource Format="MATHML"><math> <mrow> <mi mathvariant="normal">Δ</mi> <msubsup> <mi>H</mi> <mrow> <mi mathvariant="italic">el</mi> </mrow> <mrow> <mo>∘</mo> <mo>#</mo> </mrow> </msubsup> </mrow> </math></EquationSource> </InlineEquation> at 550&#xa0;mV for MOR.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Facile synthesis of novel NiCo2O4-Mn1-xCrxCo2O4 (x = 0.2, 0.6, 0.8) composites for oxygen evolution and methanol oxidation in alkaline medium

  • 期刊论文

  • 发表日期：

    2025年2月21日

查看全文
  • Reena Parihar,
  • Prakhar Mishra,
  • Yamini Singh,
  • Pradeep Kumar Yadav,
  • Narendra Kumar Singh

摘要

The electrochemical properties of spinel oxide-spinel oxide composites [NiCo2O4-Mn1-xCrxCo2O4 (x = 0.2, 0.6, 0.8)] with regard to oxygen evolution reaction (OER) and methanol oxidation reaction (MOR) have been investigated. Co-precipitation and sol–gel techniques were utilized to synthesize the materials. Fourier-transform infrared (FTIR) spectroscopy, X-Ray Diffraction (XRD) and Scanning Electron Microscopy (SEM) were employed to analyse the physicochemical properties of the synthesized materials. Electrochemical examinations such as cyclic voltammetry (CV) and Tafel experiment were performed in 1 M KOH with and without methanol at 25 °C. The electrocatalytic performance of the materials was assessed via anodic polarization curves and NiCo2O4-Mn0.2Cr0.8Co2O4 was found to be most active towards the OER (j = 33.5 mAcm−2) and NiCo2O4-Mn0.8Cr0.2Co2O4 was found to be most active towards the MOR (j = 74.3 mAcm−2) at 750 mV. The electrodes’ durability was investigated using chronoamperometric studies and electrochemically active surface area (ECSA) evaluations using Electrochemical Impedance Spectroscopy (EIS) offered further understanding into the enhancement in electrocatalytic activity. From the EIS experiment, the roughness factor for NiCo2O4-Mn0.8Cr0.2Co2O4 and NiCo2O4-Mn0.2Cr0.8Co2O4 was calculated and found to be 6.48 & 22.48, respectively in 1 M KOH. Using chronoamperometry experiment, the retained current (%) for NiCo2O4-Mn0.8Cr0.2Co2O4 and NiCo2O4-Mn0.2Cr0.8Co2O4 was found to be 27% and 41%, respectively in 1 M KOH. The interplay in the thermodynamic properties of the electrocatalyst has been also investigated for OER and MOR. It was found that the nanocomposite NiCo2O4-Mn0.8Cr0.2Co2O4 is well optimized to demand only 35 kJ mol−1 of \(\Delta H_{el}^{\circ\#}\) Δ H el ∘ # at 650 mV for OER and the nanocomposite NiCo2O4-Mn0.6Cr0.4Co2O4 demands only 45 kJ mol−1 of \(\Delta H_{el}^{\circ\#}\) Δ H el ∘ # at 550 mV for MOR.