<p>Ce<sup>4+</sup> rare earth ions mixed metal oxides with chemical composition Ce<sub>x</sub>Cu<sub>0.5</sub>Mn<sub>0.5-x</sub>O<sub>2</sub> (x = 0.0, 0.01, 0.03,0.05) synthesized by co-precipitation technique. The as-synthesized nanoparticles were further calcined for 500&#xa0;°C. The calcined binary and ternary nano oxides were characterized by powder XRD, SEM, EDX, FTIR, PL, CV, Antimicrobial and photocatalytic studies. X-ray diffraction confirmed the crystalline nature of the synthesized nano oxides with the crystalline size varying from 10 to 16&#xa0;nm. The particle size is observed to increase with Ce<sup>4+</sup> concentration. Morphology was analysed using SEM micrograph and the present elemental particles were found from EDX analysis. The confirmation of formed metal oxide bonds was done by FTIR. The PL spectra reveal strong emission peaks around 460&#xa0;nm, 540&#xa0;nm and 820&#xa0;nm. The peaks show that all the samples include defect associated peak in the visible region. Antimicrobial activity was investigated against two gram-negative (<i>klebsiella pneumoniae</i>, <i>pseudomonas aeruginosa)</i> and two gram- positive bacteria (<i>Staphylococcus aureus</i>, <i>Streptococcus pneumoniae</i>) and hence the zone of inhibition (30 μ L) was obtained. The electro chemical behaviour and hence the specific capacitance is determined from CV studies. The large value of specific capacitance shows that the synthesized nano oxides act as a promising material for electrodes. The photocatalytic degradation of synthesized Ce<sub>0.05</sub>Cu<sub>0.5</sub>Mn<sub>0.45</sub>O<sub>2</sub> nanocomposite material shows greater % of degradation efficiency (97.78%) at 100&#xa0;mg/L concentration of ARS dye.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Photocatalytic and Antimicrobial Applications of Cerium(IV) Doped Copper Manganese Oxide Nanoparticles

  • 期刊论文

  • 发表日期：

    2025年5月8日

查看全文
  • Lingeswari Chellappan,
  • Vasuki Gurusamy,
  • Sree Devi Rethnamuthu,
  • Nagarajan Muthukurumban,
  • Balu Thangaraj

摘要

Ce4+ rare earth ions mixed metal oxides with chemical composition CexCu0.5Mn0.5-xO2 (x = 0.0, 0.01, 0.03,0.05) synthesized by co-precipitation technique. The as-synthesized nanoparticles were further calcined for 500 °C. The calcined binary and ternary nano oxides were characterized by powder XRD, SEM, EDX, FTIR, PL, CV, Antimicrobial and photocatalytic studies. X-ray diffraction confirmed the crystalline nature of the synthesized nano oxides with the crystalline size varying from 10 to 16 nm. The particle size is observed to increase with Ce4+ concentration. Morphology was analysed using SEM micrograph and the present elemental particles were found from EDX analysis. The confirmation of formed metal oxide bonds was done by FTIR. The PL spectra reveal strong emission peaks around 460 nm, 540 nm and 820 nm. The peaks show that all the samples include defect associated peak in the visible region. Antimicrobial activity was investigated against two gram-negative (klebsiella pneumoniae, pseudomonas aeruginosa) and two gram- positive bacteria (Staphylococcus aureus, Streptococcus pneumoniae) and hence the zone of inhibition (30 μ L) was obtained. The electro chemical behaviour and hence the specific capacitance is determined from CV studies. The large value of specific capacitance shows that the synthesized nano oxides act as a promising material for electrodes. The photocatalytic degradation of synthesized Ce0.05Cu0.5Mn0.45O2 nanocomposite material shows greater % of degradation efficiency (97.78%) at 100 mg/L concentration of ARS dye.