<p>A self-developed tube-to-tube contact fretting wear tester was used to conduct fretting wear tests on Zr-4 fuel rods in pressurized water reactors of nuclear power plants under three fretting wear modes (tangential, radial, and dual-motion fretting) with different normal loads [<i>F</i><sub>n</sub> = 15–25 (20), 30–50 (40), and 45–75 (60) N]. The test results show that the normal load and fretting wear mode have a significant effect on the fretting wear behaviors of Zr-4 alloy tube. Comparing the different fretting wear modes, the contact surface is almost coordinated by elastic deformation under the radial fretting wear mode, with the slightest damage; for tangential fretting wear mode, the damage mechanism is mainly fatigue wear and delamination; the most severe damage was observed under the dual-motion fretting wear mode, where the wear mechanism consisted of a combination of delamination, abrasive wear, adhesive wear, and oxidative wear.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Study on the Effect of Normal Loads on the Fretting Wear Performance of Zr-4 Alloy Tubes Under Three Fretting Modes

  • 期刊论文

  • 发表日期：

    2025年2月5日

查看全文
  • Wenxin Xie,
  • Siyuan Ding,
  • Bin Rong,
  • XiZhang Wang,
  • Lei Xu,
  • JingFang Peng

摘要

A self-developed tube-to-tube contact fretting wear tester was used to conduct fretting wear tests on Zr-4 fuel rods in pressurized water reactors of nuclear power plants under three fretting wear modes (tangential, radial, and dual-motion fretting) with different normal loads [Fn = 15–25 (20), 30–50 (40), and 45–75 (60) N]. The test results show that the normal load and fretting wear mode have a significant effect on the fretting wear behaviors of Zr-4 alloy tube. Comparing the different fretting wear modes, the contact surface is almost coordinated by elastic deformation under the radial fretting wear mode, with the slightest damage; for tangential fretting wear mode, the damage mechanism is mainly fatigue wear and delamination; the most severe damage was observed under the dual-motion fretting wear mode, where the wear mechanism consisted of a combination of delamination, abrasive wear, adhesive wear, and oxidative wear.