<p>The microstructure, mechanical properties and corrosion resistance of promising medical Zn – 1% Mg – 0.1% Dy and Zn – 1% Mg – 0.1% Mn alloys after high-pressure torsion (HPT) are studied. It is shown that the HPT results in formation of an ultrafine-grained structure of α-Zn with grain size 450 – 700 nm in both alloys. The grain-boundary magnesium phase is refined to a nanosize and Mn- and Dy-enriched particles are precipitated. This refinement of the structure leads to a simultaneous increase in the strength and ductility of both alloys without changing their corrosion resistance. At the same time, the corrosion rate of the alloys both before and after the HPT does not exceed 0.35 mm/year.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Study Of Microstructure and Properties of Zn – 1% Mg – 0.1% Dy and Zn – 1% Mg – 0.1% Mn Alloys After High-Pressure Torsion

  • 期刊论文

  • 发表日期：

    2025年1月1日

查看全文
  • N. S. Martynenko,
  • D. R. Temralieva,
  • N. Yu. Tabachkova,
  • O. V. Rybalchenko,
  • E. A. Luk’yanova,
  • A. V. Koltygin,
  • S. V. Dobatkin

摘要

The microstructure, mechanical properties and corrosion resistance of promising medical Zn – 1% Mg – 0.1% Dy and Zn – 1% Mg – 0.1% Mn alloys after high-pressure torsion (HPT) are studied. It is shown that the HPT results in formation of an ultrafine-grained structure of α-Zn with grain size 450 – 700 nm in both alloys. The grain-boundary magnesium phase is refined to a nanosize and Mn- and Dy-enriched particles are precipitated. This refinement of the structure leads to a simultaneous increase in the strength and ductility of both alloys without changing their corrosion resistance. At the same time, the corrosion rate of the alloys both before and after the HPT does not exceed 0.35 mm/year.