<p>Various liquid crystal epoxy resins with liquid crystal properties are widely used as electronic packaging materials. However, most liquid crystals have specific molecular structures, and the synthesis methods and processes used are complicated and costly. In this study, 4,4′-biphenol and epichlorohydrin were used as synthetic monomers to synthesize oligomeric 4,4′-diglycidyloxybiphenyl (BP) epoxy resin containing biphenyl moieties. Moreover, the synthesis method was optimized to obtain a higher-quality product. The thermodynamic properties of the new product and the cured product of E51 epoxy resin were compared to highlight the advantages of liquid crystal epoxy resins. The results showed that the epoxy equivalent of the liquid crystal epoxy resin obtained by the optimized synthesis method was 184.4&#xa0;g/eq, which was lower than that of the liquid crystal epoxy resin synthesized by the traditional one-step method (200.2&#xa0;g/eq). Compared with the cured sample of Epoxy resin 51 (E51), its glass transition temperature (Tg) reached 277.2&#xa0;°C, the initial storage modulus was 2308&#xa0;MPa, and the initial decomposition temperature reached 389.85&#xa0;°C. Therefore, it can be concluded that optimizing the synthesis steps can improve the performance of liquid crystal epoxy resins. And compared with ordinary epoxy resins, liquid crystal epoxy resins have more excellent performance. The research results provide an optimization idea for the synthesis method of liquid crystal epoxy resins and provide data support for its application through the study of curing kinetics.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Research on the Preparation and properties of biphenol liquid crystal epoxy resin

  • 期刊论文

  • 发表日期：

    2025年10月4日

查看全文
  • Kaijie Yang,
  • Jiachun Zhong,
  • Zejun Pu,
  • Jiahong Pang,
  • Yuhao Yang,
  • Mengjie Yue

摘要

Various liquid crystal epoxy resins with liquid crystal properties are widely used as electronic packaging materials. However, most liquid crystals have specific molecular structures, and the synthesis methods and processes used are complicated and costly. In this study, 4,4′-biphenol and epichlorohydrin were used as synthetic monomers to synthesize oligomeric 4,4′-diglycidyloxybiphenyl (BP) epoxy resin containing biphenyl moieties. Moreover, the synthesis method was optimized to obtain a higher-quality product. The thermodynamic properties of the new product and the cured product of E51 epoxy resin were compared to highlight the advantages of liquid crystal epoxy resins. The results showed that the epoxy equivalent of the liquid crystal epoxy resin obtained by the optimized synthesis method was 184.4 g/eq, which was lower than that of the liquid crystal epoxy resin synthesized by the traditional one-step method (200.2 g/eq). Compared with the cured sample of Epoxy resin 51 (E51), its glass transition temperature (Tg) reached 277.2 °C, the initial storage modulus was 2308 MPa, and the initial decomposition temperature reached 389.85 °C. Therefore, it can be concluded that optimizing the synthesis steps can improve the performance of liquid crystal epoxy resins. And compared with ordinary epoxy resins, liquid crystal epoxy resins have more excellent performance. The research results provide an optimization idea for the synthesis method of liquid crystal epoxy resins and provide data support for its application through the study of curing kinetics.