<p>In this study, a series of microporous carbon bead adsorbents were prepared via the hydrothermal activation of acetyl-rich cellulose acetate with potassium hydroxide at elevated temperatures. The adsorbents were characterized through the use of a range of analytical techniques, including scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), infrared spectroscopy (FT-IR), X-ray diffraction (XRD), HCS thermodynamic software, and Raman spectroscopy (Raman). The results showed that the surface pores of carbon microspheres were uniformly distributed with homogeneous narrow microporous structure (0.50–1.14&#xa0;nm) when the acetyl group content was 54.5%, and the narrow micropores pore volume of the adsorbent increased with the increase of the acetyl group content, so that the CAC-54.5–700 had the highest V<sub>0.50–1.14&#xa0;nm</sub> (0.47&#xa0;m<sup>3</sup>/g), which provided an excellent adsorption site for the adsorption of CH<sub>4</sub> and CO<sub>2</sub>, and at the same time The acetyl group provides more oxygen-containing functional groups (C–O), which improves the adsorption capacity and regeneration ability of the adsorbent. The carbon material CAC-54.5–700 showed excellent selectivity for CO<sub>2</sub> and CH<sub>4</sub> adsorption up to 6.05&#xa0;mmol/g and 3.18&#xa0;mmol/g, as well as for CH<sub>4</sub>/N<sub>2</sub> (21.6), and the adsorption process conformed to the Freundlich model. After several adsorption–desorption cycles, the adsorption penetration time of CH<sub>4</sub> was stabilized at 804&#xa0;s/g, and the dynamic adsorption amount of CO<sub>2</sub> was stabilized at 1.6&#xa0;mmol/g, indicating that the prepared acetylated porous carbon has good potentials for application in CH<sub>4</sub> and CO<sub>2</sub> enrichment.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Acetylated narrow micropores carbon for CO2 and CH4 adsorption

  • 期刊论文

  • 发表日期：

    2025年1月3日

查看全文
  • Honglong Xie,
  • Dailiu Hu,
  • Nian He,
  • E. Yang,
  • Zili Wang,
  • Shisong Yang,
  • Ran Zhu,
  • Hongyan Pan,
  • Qian Lin

摘要

In this study, a series of microporous carbon bead adsorbents were prepared via the hydrothermal activation of acetyl-rich cellulose acetate with potassium hydroxide at elevated temperatures. The adsorbents were characterized through the use of a range of analytical techniques, including scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), infrared spectroscopy (FT-IR), X-ray diffraction (XRD), HCS thermodynamic software, and Raman spectroscopy (Raman). The results showed that the surface pores of carbon microspheres were uniformly distributed with homogeneous narrow microporous structure (0.50–1.14 nm) when the acetyl group content was 54.5%, and the narrow micropores pore volume of the adsorbent increased with the increase of the acetyl group content, so that the CAC-54.5–700 had the highest V0.50–1.14 nm (0.47 m3/g), which provided an excellent adsorption site for the adsorption of CH4 and CO2, and at the same time The acetyl group provides more oxygen-containing functional groups (C–O), which improves the adsorption capacity and regeneration ability of the adsorbent. The carbon material CAC-54.5–700 showed excellent selectivity for CO2 and CH4 adsorption up to 6.05 mmol/g and 3.18 mmol/g, as well as for CH4/N2 (21.6), and the adsorption process conformed to the Freundlich model. After several adsorption–desorption cycles, the adsorption penetration time of CH4 was stabilized at 804 s/g, and the dynamic adsorption amount of CO2 was stabilized at 1.6 mmol/g, indicating that the prepared acetylated porous carbon has good potentials for application in CH4 and CO2 enrichment.