<p>Polymer dielectric film capacitors serve as crucial energy storage devices in modern electronic systems. However, the conventional dielectric materials have high conduction loss at elevated temperature. Hence, we propose a synergistic regulation strategy based on molecular traps to improve the high-temperature energy storage performance of cyclic olefin copolymer (COC). Firstly, the polar group maleic anhydride (MAH) is introduced into the COC molecular chain through the structure design, which creates deep energy traps to suppress intrachain charge transport. Furthermore, the intermolecular charge trap is constructed by introducing molecular semiconductor PCBM, which has high electron affinity energy (2.6–2.8&#xa0;eV), realizing the intramolecular and intermolecular charge transport co-inhibition. The results show that COC-g-MAH/PCBM-0.10 exhibits a maximum discharge energy density (<i>U</i><sub>e</sub>) of 4.47&#xa0;J/cm<sup>3</sup> under 620&#xa0;kV/mm at 120&#xa0;℃, and the efficiency (<i>η</i>) above 90%, which is 85% higher than COC. It’s noteworthy that at 120&#xa0;℃ and 500&#xa0;kV/mm, after 50,000 charge–discharge cycles, the <i>η</i> of COC-g-MAH/PCBM-0.10 still remains at 92%, proving it has excellent high-temperature cycling stability. This strategy based on trap design provides a new paradigm for advanced dielectric materials with high energy storage performance and stability, demonstrating significant potential for practical applications.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Enhanced high-temperature energy storage performance of COC by suppressing carrier transport

  • 期刊论文

  • 发表日期：

    2025年4月5日

查看全文
  • Yiwei Zhang,
  • Jiaqi Zhang,
  • Qiyue Zhang,
  • Changhai Zhang,
  • Tiandong Zhang,
  • Yongquan Zhang,
  • Yue Zhang,
  • Qingguo Chi

摘要

Polymer dielectric film capacitors serve as crucial energy storage devices in modern electronic systems. However, the conventional dielectric materials have high conduction loss at elevated temperature. Hence, we propose a synergistic regulation strategy based on molecular traps to improve the high-temperature energy storage performance of cyclic olefin copolymer (COC). Firstly, the polar group maleic anhydride (MAH) is introduced into the COC molecular chain through the structure design, which creates deep energy traps to suppress intrachain charge transport. Furthermore, the intermolecular charge trap is constructed by introducing molecular semiconductor PCBM, which has high electron affinity energy (2.6–2.8 eV), realizing the intramolecular and intermolecular charge transport co-inhibition. The results show that COC-g-MAH/PCBM-0.10 exhibits a maximum discharge energy density (Ue) of 4.47 J/cm3 under 620 kV/mm at 120 ℃, and the efficiency (η) above 90%, which is 85% higher than COC. It’s noteworthy that at 120 ℃ and 500 kV/mm, after 50,000 charge–discharge cycles, the η of COC-g-MAH/PCBM-0.10 still remains at 92%, proving it has excellent high-temperature cycling stability. This strategy based on trap design provides a new paradigm for advanced dielectric materials with high energy storage performance and stability, demonstrating significant potential for practical applications.