<p>Herein, we synthesized bismuth (Bi)-doped CoFe<sub>2</sub>O<sub>4</sub> nanoparticles using the sol–gel auto-combustion method. X-ray diffraction pattern confirmed the formation of a cubic spinel structure in all samples where crystallite size ranged between 37.03 and 30.03&#xa0;nm. The lattice parameter ranged between 8.393 and 8.409&#xa0;Å except for the composition, <i>x</i> = 0.1. Fourier transform infrared spectra revealed the presence of octahedral and tetrahedral vibrational bands of 480–473&#xa0;cm<sup>−1</sup> and 605–588&#xa0;cm<sup>−1</sup>, respectively. The Scanning Electron Microscopy and Transmission Electron Microscopy revealed the formation of irregular grains. Energy-dispersive X-ray spectra validated the chemical purity of all the samples. The magnetic studies revealed an increase in saturation magnetization from 54.828 to 79.713&#xa0;emu/g with the increase in doping concentration due to the spin canting effect. The microwave properties showed a decrease in magnetic loss from 0.198 to 0.132 with an increase in Bi content, whereas dielectric loss increased from 0.242 to 0.422. EMI shielding analysis showed an increase in the shielding effect due to reflection from 9.398 to 10.373&#xa0;dB with increasing doping concentration. Thus, the prepared samples paved a way for the application of Bi-doped cobalt ferrite in EMI shielding with improved magnetic and electric properties at high frequency.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Bi-doped cobalt ferrite nanoparticles for electromagnetic interference (EMI) shielding applications

  • 期刊论文

  • 发表日期：

    2025年3月17日

查看全文
  • Rahul Kalia,
  • Ankush Chauhan,
  • Rohit Jasrotia,
  • Muhammad Farzik Ijaz,
  • Khalid Mujassam Batoo,
  • Ritesh Verma

摘要

Herein, we synthesized bismuth (Bi)-doped CoFe2O4 nanoparticles using the sol–gel auto-combustion method. X-ray diffraction pattern confirmed the formation of a cubic spinel structure in all samples where crystallite size ranged between 37.03 and 30.03 nm. The lattice parameter ranged between 8.393 and 8.409 Å except for the composition, x = 0.1. Fourier transform infrared spectra revealed the presence of octahedral and tetrahedral vibrational bands of 480–473 cm−1 and 605–588 cm−1, respectively. The Scanning Electron Microscopy and Transmission Electron Microscopy revealed the formation of irregular grains. Energy-dispersive X-ray spectra validated the chemical purity of all the samples. The magnetic studies revealed an increase in saturation magnetization from 54.828 to 79.713 emu/g with the increase in doping concentration due to the spin canting effect. The microwave properties showed a decrease in magnetic loss from 0.198 to 0.132 with an increase in Bi content, whereas dielectric loss increased from 0.242 to 0.422. EMI shielding analysis showed an increase in the shielding effect due to reflection from 9.398 to 10.373 dB with increasing doping concentration. Thus, the prepared samples paved a way for the application of Bi-doped cobalt ferrite in EMI shielding with improved magnetic and electric properties at high frequency.