<p>In order to optimize the structure and magnetic properties of Ba-CO nano-ferrite, rare-earth ions-doped Ba<sub>0.2</sub>Co<sub>0.8</sub>Fe<sub>2-x</sub>RE<sub>x</sub>O<sub>4</sub> (RE = Sm, Ce, La and x = 0.02) nanopowder was prepared by sol–gel method at 950&#xa0;°C. X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FT-IR) were used for the structural analysis. The presence of few additional phases (BaFe<sub>2</sub>O<sub>4</sub>) was found in the doped samples. After the RE ions doping, the lattice constant calculated from the XRD patterns increased to 8.3791&#xa0;Å. The morphology of the material was studied using scanning electron microscopy (SEM), transmission electron microscopy (TEM), and selected area electron diffraction (SAED). Energy-dispersive spectrometer analysis (EDS) confirmed that there are corresponding rare-earth elements, as well as Ba, Co, and O elements in the sample. The binding energy of La-doped barium cobalt nano-ferrite was studied by X-ray photoelectron spectroscopy. The peak of Ba<sup>2+</sup> 3<i>d</i><sub><i>3/2</i></sub> is observed at the binding energy of 795.22&#xa0;eV, while the peak of Ba<sup>2+</sup> 3<i>d</i><sub><i>5/2</i></sub> appears at the binding energy of 779.97&#xa0;eV. Co<sup>2+</sup> and Fe<sup>3+</sup> contributions to octahedron and tetrahedron are calculated. The magnetic properties of the samples were studied using a vibrating sample magnetometer (VSM). We&#xa0;found that the saturation magnetization (<i>M</i>s) of Ba<sub>0.2</sub>Co<sub>0.8</sub>Fe<sub>2</sub>La<sub>0.02</sub>O<sub>4</sub> nano-ferrite was higher compared to other samples, Which provides references for other investigators.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Impact of rare-earth ions (Ce, La, Sm) doping on the lattice structure and magnetic characteristics of barium cobalt nano-ferrite

  • 期刊论文

  • 发表日期：

    2025年3月3日

查看全文
  • Zhaxi Suonan,
  • Yingqiang Han

摘要

In order to optimize the structure and magnetic properties of Ba-CO nano-ferrite, rare-earth ions-doped Ba0.2Co0.8Fe2-xRExO4 (RE = Sm, Ce, La and x = 0.02) nanopowder was prepared by sol–gel method at 950 °C. X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FT-IR) were used for the structural analysis. The presence of few additional phases (BaFe2O4) was found in the doped samples. After the RE ions doping, the lattice constant calculated from the XRD patterns increased to 8.3791 Å. The morphology of the material was studied using scanning electron microscopy (SEM), transmission electron microscopy (TEM), and selected area electron diffraction (SAED). Energy-dispersive spectrometer analysis (EDS) confirmed that there are corresponding rare-earth elements, as well as Ba, Co, and O elements in the sample. The binding energy of La-doped barium cobalt nano-ferrite was studied by X-ray photoelectron spectroscopy. The peak of Ba2+ 3d3/2 is observed at the binding energy of 795.22 eV, while the peak of Ba2+ 3d5/2 appears at the binding energy of 779.97 eV. Co2+ and Fe3+ contributions to octahedron and tetrahedron are calculated. The magnetic properties of the samples were studied using a vibrating sample magnetometer (VSM). We found that the saturation magnetization (Ms) of Ba0.2Co0.8Fe2La0.02O4 nano-ferrite was higher compared to other samples, Which provides references for other investigators.