<p>Pb-based perovskites with multiple cations are fascinating materials showing various phenomena such as high piezoelectric, electromechanical, and relaxor properties. While chemical disordering accompanied by polar nanoregions and nanosized domains is commonly believed to cause the relaxor nature, little is known about ferroelectric microstructures of chemically ordered Pb-based perovskites. In this study, we discovered intriguing meandering ferroelectric domains in chemically ordered ferroelectric Pb(Sc<sub>1/2</sub>Nb<sub>1/2</sub>)O<sub>3</sub> using in situ transmission electron microscopy with dark-field imaging. Observation results demonstrate that electric polarization can fluctuate around the [111] direction despite the formation of long-range ordered rhombohedral domains, which results in unique weak relaxor properties. In situ imaging upon heating successfully reveals the dynamic behavior of domain-wall movements with lattice distortion and paraelectric–ferroelectric phase coexistence in the vicinity of the Curie temperature, indicating a discontinuous phase transition. Our research provides new insights into the effect of chemical ordering on ferroelectric nanodomains.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Characteristic ferroelectric domains and their dynamic behavior in ordered Pb(Sc1/2Nb1/2)O3

  • 期刊论文

  • 发表日期：

    2025年5月28日

查看全文
  • Hiroshi Nakajima,
  • Satoshi Hiroi,
  • Hirofumi Tsukasaki,
  • Yonghong Bing,
  • Stéphane Grenier,
  • Zuo-Guang Ye,
  • Pierre-Eymeric Janolin,
  • Shigeo Mori

摘要

Pb-based perovskites with multiple cations are fascinating materials showing various phenomena such as high piezoelectric, electromechanical, and relaxor properties. While chemical disordering accompanied by polar nanoregions and nanosized domains is commonly believed to cause the relaxor nature, little is known about ferroelectric microstructures of chemically ordered Pb-based perovskites. In this study, we discovered intriguing meandering ferroelectric domains in chemically ordered ferroelectric Pb(Sc1/2Nb1/2)O3 using in situ transmission electron microscopy with dark-field imaging. Observation results demonstrate that electric polarization can fluctuate around the [111] direction despite the formation of long-range ordered rhombohedral domains, which results in unique weak relaxor properties. In situ imaging upon heating successfully reveals the dynamic behavior of domain-wall movements with lattice distortion and paraelectric–ferroelectric phase coexistence in the vicinity of the Curie temperature, indicating a discontinuous phase transition. Our research provides new insights into the effect of chemical ordering on ferroelectric nanodomains.