<p>The valorization of agricultural waste is essential for promoting sustainability, economic growth, and environmental mitigation. In this study, henequen bagasse a waste of the henequen agroindustry was utilized as a lignocellulosic material for cellulose extraction and use it in obtaining cellulose–acrylic composite films. Two methods were employed for cellulose obtaining: the alkaline hydrothermal process (AHTP) and the alkaline extraction process (AEP). The resulting cellulose pulp was analyzed in terms of yield, particle size, crystallinity, and morphology. The results indicated that the AEP method yielded a higher efficiency (43%) and aspect ratio (<InlineEquation ID="IEq1"> <InlineMediaObject> <ImageObject Color="BlackWhite" FileRef="10570_2025_6715_Article_IEq1.gif" Format="GIF" Height="19" Rendition="HTML" Resolution="72" Type="Linedraw" Width="74" /> </InlineMediaObject> <EquationSource Format="TEX">\(L/D = 73\)</EquationSource> <EquationSource Format="MATHML"><math> <mrow> <mi>L</mi> <mo stretchy="false">/</mo> <mi>D</mi> <mo>=</mo> <mn>73</mn> </mrow> </math></EquationSource> </InlineEquation>), whereas the AHTP method yielded 37% with an aspect ratio of 55. In terms of crystallinity, the AHTP method produced cellulose with 63% crystallinity, exhibiting a cellulose I structure, while the AEP method resulted in 44% crystallinity with a partial conversion from cellulose I to cellulose II. Composites were prepared dispersing cellulose in a commercial acrylic base latex (AF). Thermogravimetric analysis curves showed a single-step degradation at approximately 377&#xa0;°C for cellulose and 400&#xa0;°C for AF. The inclusion of cellulose did not affect the thermal stability of AF. Finally, the effect of cellulose incorporation on the mechanical properties of the reinforced material was evaluated. The highest elastic modulus (111&#xa0;MPa) and ultimate tensile strength (6&#xa0;MPa) were obtained for the composite reinforced with AHTP-derived cellulose at 10&#xa0;wt%. However, a significant reduction in elongation at break was observed, decreasing from 435 to 77%.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Valorization of henequen bagasse via cellulose extraction: influence of the extraction method on the properties of cellulose-reinforced composite films

  • 期刊论文

  • 发表日期：

    2025年8月17日

查看全文
  • I. Y. Forero-Sandoval,
  • S. Duarte-Aranda,
  • G. Canche-Escamilla

摘要

The valorization of agricultural waste is essential for promoting sustainability, economic growth, and environmental mitigation. In this study, henequen bagasse a waste of the henequen agroindustry was utilized as a lignocellulosic material for cellulose extraction and use it in obtaining cellulose–acrylic composite films. Two methods were employed for cellulose obtaining: the alkaline hydrothermal process (AHTP) and the alkaline extraction process (AEP). The resulting cellulose pulp was analyzed in terms of yield, particle size, crystallinity, and morphology. The results indicated that the AEP method yielded a higher efficiency (43%) and aspect ratio ( \(L/D = 73\) L / D = 73 ), whereas the AHTP method yielded 37% with an aspect ratio of 55. In terms of crystallinity, the AHTP method produced cellulose with 63% crystallinity, exhibiting a cellulose I structure, while the AEP method resulted in 44% crystallinity with a partial conversion from cellulose I to cellulose II. Composites were prepared dispersing cellulose in a commercial acrylic base latex (AF). Thermogravimetric analysis curves showed a single-step degradation at approximately 377 °C for cellulose and 400 °C for AF. The inclusion of cellulose did not affect the thermal stability of AF. Finally, the effect of cellulose incorporation on the mechanical properties of the reinforced material was evaluated. The highest elastic modulus (111 MPa) and ultimate tensile strength (6 MPa) were obtained for the composite reinforced with AHTP-derived cellulose at 10 wt%. However, a significant reduction in elongation at break was observed, decreasing from 435 to 77%.