<p>Radiation-related dental caries (RRC) is a rapidly progressing and treatment-resistant condition commonly observed after head and neck radiotherapy. It has traditionally been attributed to radiation-induced salivary gland dysfunction; however, RRC often develops even when appropriate oral care is provided, including fluoride application and regular hygiene practices. This clinical inconsistency suggests that salivary dysfunction alone cannot fully explain the onset and severity of RRC. The direct physicochemical effects of radiation on the organic and inorganic components of dental hard tissues remain poorly understood. In this study, extracted human third molars were subjected to a clinical IMRT protocol, using either a single high dose (20&#xa0;Gy × 1) or a fractionated regimen (2&#xa0;Gy/day × 35, total 70&#xa0;Gy). We then evaluated radiation-induced changes in tooth structure by measuring Vickers microhardness, acid resistance (calcium elution), collagen degradation (autofluorescence), and internal dentin pH. Radiation exposure significantly altered enamel hardness: it increased after 20&#xa0;Gy but decreased following 70&#xa0;Gy. Calcium release increased in crown enamel (70&#xa0;Gy) and root dentin (20&#xa0;Gy), while decreasing in crown dentin (20&#xa0;Gy). Autofluorescence imaging showed a significant reduction in dentinal collagen after fractionated exposure. Both groups exhibited an alkaline shift in dentin pH, more pronounced in the single-dose group. These findings provide physicochemical evidence for a non-salivary mechanism contributing to RRC. To effectively prevent RRC, additional strategies to reduce direct radiation damage to dental tissues may be necessary alongside conventional salivary-focused approaches.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Direct radiation damage to human tooth under IMRT for head and neck cancer: physicochemical evidence supporting a non-salivary mechanism for radiation-related caries

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2025年12月15日

查看全文
  • Toru Tamahara,
  • Atsumu Kouketsu

摘要

Radiation-related dental caries (RRC) is a rapidly progressing and treatment-resistant condition commonly observed after head and neck radiotherapy. It has traditionally been attributed to radiation-induced salivary gland dysfunction; however, RRC often develops even when appropriate oral care is provided, including fluoride application and regular hygiene practices. This clinical inconsistency suggests that salivary dysfunction alone cannot fully explain the onset and severity of RRC. The direct physicochemical effects of radiation on the organic and inorganic components of dental hard tissues remain poorly understood. In this study, extracted human third molars were subjected to a clinical IMRT protocol, using either a single high dose (20 Gy × 1) or a fractionated regimen (2 Gy/day × 35, total 70 Gy). We then evaluated radiation-induced changes in tooth structure by measuring Vickers microhardness, acid resistance (calcium elution), collagen degradation (autofluorescence), and internal dentin pH. Radiation exposure significantly altered enamel hardness: it increased after 20 Gy but decreased following 70 Gy. Calcium release increased in crown enamel (70 Gy) and root dentin (20 Gy), while decreasing in crown dentin (20 Gy). Autofluorescence imaging showed a significant reduction in dentinal collagen after fractionated exposure. Both groups exhibited an alkaline shift in dentin pH, more pronounced in the single-dose group. These findings provide physicochemical evidence for a non-salivary mechanism contributing to RRC. To effectively prevent RRC, additional strategies to reduce direct radiation damage to dental tissues may be necessary alongside conventional salivary-focused approaches.