<p>The rising demand for cutting-edge microwave absorbers in stealth technology and innovative communication systems necessitates the production of materials with enhanced electromagnetic wave absorption and enhanced dielectric and magnetic properties. Herein, this study explores the potential of the M-type hexagonal nanoferrite composite, BaTiCo<sub>0.5</sub>Mn<sub>0.3</sub>Ni<sub>0.2</sub>Fe<sub>10</sub>O<sub>19</sub>, for microwave absorption applications. The composite was prepared using a nano-alloying thermo-mechanical process, incorporating calcination (C), sintering (S), and high-energy nano-alloying (H) techniques. The result of electromagnetic (EM) parameters shows that the composite exhibits a superior reflection loss (R<sub>L</sub>) of -38.28 dB at 12.9 GHz with a thickness of 2&#xa0;mm in the CSH composite. The synergistic approach of calcination, sintering, and nano-alloying enhances crystallinity while preserving the nanometric microstructure, resulting in a large surface area and improved exchange coupling, positively influencing microwave absorption properties. The substitution of elements increases permittivity (ε’) to approximately 8.6 and permeability (µ’) to 1.43, respectively, resulting in enhanced dielectric polarization and superior microwave absorption. Also, the results demonstrate that BaTiCo<sub>0.5</sub>Mn<sub>0.3</sub>Ni<sub>0.2</sub>Fe<sub>10</sub>O<sub>19</sub>, with its high dielectric loss (ε’’ up to 0.45 at 15.9 GHz) and high magnetic loss (µ’’ up to 0.79 at 12.6&#xa0;GHz), can serve as an effective ferrite-based microwave absorber in epoxy composites. This ferrite nanoparticle composite’s outstanding microwave absorption performance in the Ku-bands makes it a promising material for applications in stealth technology and advanced communication systems.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Synthesis and characterization of M-type; BaTiCo0.5Mn0.3Ni0.2Fe10O19 nano ferrite composite via synergistic nano-alloying and thermal processing and its application for microwave absorption

  • 期刊论文

  • 发表日期：

    2025年9月29日

查看全文
  • Chen Hongxu,
  • Raba’ah Syahidah Azis,
  • Ismayadi Ismail,
  • Kamil Kayode Katibi,
  • Mohamad Hafiz Mohd Zaid,
  • Khamirul Amin Matori,
  • Yusuf Sani,
  • Norazila Ibrahim,
  • Chen Soo Kien,
  • Lim Kean Pah,
  • Mohd Mustafa Awang Kechik

摘要

The rising demand for cutting-edge microwave absorbers in stealth technology and innovative communication systems necessitates the production of materials with enhanced electromagnetic wave absorption and enhanced dielectric and magnetic properties. Herein, this study explores the potential of the M-type hexagonal nanoferrite composite, BaTiCo0.5Mn0.3Ni0.2Fe10O19, for microwave absorption applications. The composite was prepared using a nano-alloying thermo-mechanical process, incorporating calcination (C), sintering (S), and high-energy nano-alloying (H) techniques. The result of electromagnetic (EM) parameters shows that the composite exhibits a superior reflection loss (RL) of -38.28 dB at 12.9 GHz with a thickness of 2 mm in the CSH composite. The synergistic approach of calcination, sintering, and nano-alloying enhances crystallinity while preserving the nanometric microstructure, resulting in a large surface area and improved exchange coupling, positively influencing microwave absorption properties. The substitution of elements increases permittivity (ε’) to approximately 8.6 and permeability (µ’) to 1.43, respectively, resulting in enhanced dielectric polarization and superior microwave absorption. Also, the results demonstrate that BaTiCo0.5Mn0.3Ni0.2Fe10O19, with its high dielectric loss (ε’’ up to 0.45 at 15.9 GHz) and high magnetic loss (µ’’ up to 0.79 at 12.6 GHz), can serve as an effective ferrite-based microwave absorber in epoxy composites. This ferrite nanoparticle composite’s outstanding microwave absorption performance in the Ku-bands makes it a promising material for applications in stealth technology and advanced communication systems.