<p>A series of FeCl<sub>3</sub> doped MIL-101(Cr)/silicon nanoporous pillar array (FeCl<sub>3</sub>/MIL-101(Cr)/Si-NPA) humidity sensors were prepared by growing FeCl<sub>3</sub> doped MIL-101(Cr) on Si-NPA via a facile spin-coating method. Systematically evaluation of capacitive sensing performance demonstrated that FeCl<sub>3</sub> incorporation significantly enhanced humidity sensitivity. This improvement can be attributed to the increased hydrophilicity of the MIL-101(Cr)/Si-NPA composite membranes induced by FeCl<sub>3</sub>, as confirmed by the water contact angle test results. Notably, the 8 wt.% FeCl<sub>3</sub>/MIL-101(Cr)/Si-NPA humidity sensor exhibited the best comprehensive sensing properties, with excellent linearity (R<sup>2</sup> = 0.991) in the 11–75% relative humidity (RH) range. The capacitance of the humidity sensor increased by nearly three orders of magnitude from 11% RH to 75% RH at 300&#xa0;Hz. Additionally, the humidity sensor displayed fast response (46&#xa0;s) and recovery (6&#xa0;s) times, as well as excellent reproducibility. The sensing mechanism was explored through the analysis of complex impedance curves. These finding indicate that the 8 wt.% FeCl<sub>3</sub>/MIL-101(Cr)/Si-NPA sensor holds considerable promise for humidity sensing applications.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Morphology of MIL-101(Cr) and improvement of humidity sensing performance by introducing FeCl3

  • 期刊论文

  • 发表日期：

    2025年5月6日

查看全文
  • Hongxin Cai,
  • Hang Yu,
  • Yuanyuan Liu,
  • Lingling Yan,
  • Liang Chen,
  • Qiang Hu,
  • Lingli Wang,
  • Bin Li

摘要

A series of FeCl3 doped MIL-101(Cr)/silicon nanoporous pillar array (FeCl3/MIL-101(Cr)/Si-NPA) humidity sensors were prepared by growing FeCl3 doped MIL-101(Cr) on Si-NPA via a facile spin-coating method. Systematically evaluation of capacitive sensing performance demonstrated that FeCl3 incorporation significantly enhanced humidity sensitivity. This improvement can be attributed to the increased hydrophilicity of the MIL-101(Cr)/Si-NPA composite membranes induced by FeCl3, as confirmed by the water contact angle test results. Notably, the 8 wt.% FeCl3/MIL-101(Cr)/Si-NPA humidity sensor exhibited the best comprehensive sensing properties, with excellent linearity (R2 = 0.991) in the 11–75% relative humidity (RH) range. The capacitance of the humidity sensor increased by nearly three orders of magnitude from 11% RH to 75% RH at 300 Hz. Additionally, the humidity sensor displayed fast response (46 s) and recovery (6 s) times, as well as excellent reproducibility. The sensing mechanism was explored through the analysis of complex impedance curves. These finding indicate that the 8 wt.% FeCl3/MIL-101(Cr)/Si-NPA sensor holds considerable promise for humidity sensing applications.