<p>Scots pine was subjected to radial compression at 160&#xa0;°C and heat treatment at 180–220&#xa0;°C using hot pressing to produce compressed wood and thermally compressed wood (heartwood and sapwood). Then, the macromolecular structure changes of modified wood without destruction were analyzed using high-resolution 2D HSQC NMR. After heat treatment, the contour signals in NMR spectra evidently reduced. Its reduction mainly came from side-chain cleavage of <i>O</i>-acetylated galactoglucomannans (GGMs) and 4-<i>O</i>-methyl-gluconoxylans (MGXs) in hemicellulose. Moreover, the thermal stability of GGMs was lower than that of MGXs. Specifically, the thermal stability order of monosaccharides in heartwood and sapwood should be as follows: glucose &gt; xylose &gt; mannose &gt; 2-<i>O</i>- and 3-<i>O</i>-Ac- Man<i>p</i> &gt; galactose &gt; 4-<i>O</i>-methyl-α-D-glucuronic acid ≥ arabinose. At 220&#xa0;°C, hemicellulose only left minor xylan and mannan. Conversely, the change of cellulose structure was not obvious. NMR spectra indicated high temperature caused the breaking of β-O-4, β-5, and α-O-4 bonds, leading to the mass loss of lignin.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

In situ analysis of chemical changes of thermally compressed wood by 2D NMR

  • 期刊论文

  • 发表日期：

    2025年2月7日

查看全文
  • Lili Li,
  • Xiaofei Shan,
  • Yali Shao,
  • Jianfang Yu,
  • Wenwen Liu,
  • Zhiying Luo,
  • Ximing Wang

摘要

Scots pine was subjected to radial compression at 160 °C and heat treatment at 180–220 °C using hot pressing to produce compressed wood and thermally compressed wood (heartwood and sapwood). Then, the macromolecular structure changes of modified wood without destruction were analyzed using high-resolution 2D HSQC NMR. After heat treatment, the contour signals in NMR spectra evidently reduced. Its reduction mainly came from side-chain cleavage of O-acetylated galactoglucomannans (GGMs) and 4-O-methyl-gluconoxylans (MGXs) in hemicellulose. Moreover, the thermal stability of GGMs was lower than that of MGXs. Specifically, the thermal stability order of monosaccharides in heartwood and sapwood should be as follows: glucose > xylose > mannose > 2-O- and 3-O-Ac- Manp > galactose > 4-O-methyl-α-D-glucuronic acid ≥ arabinose. At 220 °C, hemicellulose only left minor xylan and mannan. Conversely, the change of cellulose structure was not obvious. NMR spectra indicated high temperature caused the breaking of β-O-4, β-5, and α-O-4 bonds, leading to the mass loss of lignin.